Abstract:The high-entropy alloy coatings of FeCoCrNiCuB x (x = 0, 0.1, 0.3, 0.5, x values are molar ratios) were prepared on the surface of Q235 steel by laser cladding. The microstructure, microhardness, and surface energy of the FeCoCrNiCuB x coatings were investigated, and the tribological property and wear mechanism of the composite coatings at room temperature (RT) and 600 °C(HT) were analyzed. The FeCoCrNiCu coating consists of a single FCC-type solid solution. When x = 0.3, 0.5, the composite coatings appear the Cr 2 B phase. The x = 0.5 (B5) coating has the lowest surface energy (27.45mN/m), which is one of the reasons it has excellent tribological properties. The tribological properties of FeCoCrNiCuB x composite coatings were improved at both RT and HT. The B5 coating has excellent tribology at both RT and HT. At RT, the wear resistance of the B5 coating (wear rate is 8.54 ×10 −5 mm 3 /N∙m, coefficient of friction (COF) is 0.51) was improved by 54.79%, 50.89%, and 12.86% compared with x = 0(HEA), x = 0.1(B1), and x = 0.3(B3), respectively, the COF reduced by 42.69%, 41.39%, 22.73%. At HT the wear resistance of the B5 coating (wear rate is 6.69 ×10 −5 mm 3 /N∙m, COF is 0.24) was increased by 71.53%, 52.91%, and 49.42% compared to HEA, B1, and B3, respectively, the COF reduced by 29.41%, 25.00%, 17.24%. The wear mechanisms of coatings that add B element at RT are abrasive wear and fatigue wear, and at HT are mainly oxidative wear, moderate abrasive wear and fatigue wear.B 2 O 3 melts at HT to form a low-viscosity liquid that forms a lubricating film that isolates the contact surfaces and reduces direct contact and adhesion. This is the main reason for the excellent friction properties of B5 coating at HT.

Study on Microstructure and Compressive Properties of Fe-C-W-Cr-V-Nb Coating with Boron Addition

Effect of Process Parameters on Microstructure and Properties of AlCoCrFeNi-WC-WS2 Composite Coating Prepared by Laser Cladding

Influence of In-Situ Synthesized Carboborides on Microstructure Evolution and the Wear Resistance of Laser Clad Fe-base Composite Coatings

Effect of boron on the microstructural evolution and wear resistance of high-hardness Fe-based alloy coatings prepared by laser cladding

Effect of WC–Co addition on tribological and cracking behavior of laser cladded Fe-based amorphous/crystalline composite coatings

Microstructure and Wear Resistance of Laser Clad CoCrFeNiTiNbBx High Entropy Alloy Coatings

Microstructure and Property of Fe–Co–B–Si–C–Nb Amorphous Composite Coating Fabricated by Laser Cladding Process

The collaborative effect of carbon-borides and the redistribution of Ni, Cr and Mo on the corrosion and wear resistance of NiCrMoCB coatings

Effect of NbC in-situ synthesis on the microstructure and properties of pre-placed WCoB-TiC coating by laser cladding

Effect of Boron Concentration in the Fe-Cr-Mo-(B,C) Hardfacing Alloys on the Microstructure and Mechanical Properties

Effects of Boron Content on Microstructure and Wear Properties of FeCoCrNiBx High-Entropy Alloy Coating by Laser Cladding

Microstructure and Wear Resistance of Fe-Cr-Mo-Co-C-B Amorphous Composite Coatings Synthesized by Laser Cladding

Effect of boron on the microstructures and properties of 17-4PH/TiC coatings by laser cladding

Effects of NbC content on microstructural evolution and mechanical properties of laser cladded Fe50Mn30Co10Cr10-xNbC composite coatings

Fabrication of Fe-based amorphous composite coating by laser cladding

Effect of in Situ NbC on Microstructure and Wear Properties of Laser Cladding Co-Based Coatings

Effect of B addition on the microstructure and tribological properties of laser cladding FeCoCrNiCu composite coatings

Microstructure and properties of laser clad Fe-based amorphous alloy coatings containing Nb powder

Effects of B contents on the microstructure and wear resistance of hypereutectic Fe-Cr-C hardfacing alloy coating

Residual Stress Distribution and Wear Behavior in Multi-Pass Laser Cladded Fe-based Coating Reinforced by M3(C, B)

Microstructure and wear resistance of laser cladding FeNiCrMo-WC composite coating