Microstructure and wear resistance of laser cladding FeNiCrMo-WC composite coating

YIN Ze-liang,CUI Hong-zhi,SONG Xiao-jie,LI Bao-cheng,ZHAO Xiao-feng

DOI: https://doi.org/10.13289/j.issn.1009-6264.2022-0504

2023-01-01

Abstract:WC ceramic particle reinforced FeCrNiMo-WC composite coatings were prepared on Q235 steel surface by laser cladding technology. The effect of WC content on microstructure and wear resistance of the coatings was studied by means of phase composition analysis, microstructure characterization, mechanical properties testing and friction and wear experiments. The results show that besides FCC+WC, the main phase of the coatings has a network eutectic structure, which is composed of FCC and M 6 C carbide phases with alternating lamellar distribution, and the lamellar spacing is about 100 nm. With the increase of WC content, the volume fraction of eutectic structure increases, and the microstructure of eutectic structure+WC ceramic particles is gradually formed in the coatings. The addition of WC ceramic particles significantly improves the hardness and wear resistance of the coatings. When the WC content is 40 mass%, the hardness of the coating is 55.9 HRC, and the wear resistance is the best, with the minimum volume wear rate of 2.17×10 -5 mm~3/（N·m）. The hardness, strength and toughness of the coatings are improved synergistically by large WC particles and FCC+M 6 C eutectic with alternating hard lamella and soft lamella. At the same time, the M 6 C phase has the function of reducing wear, which leading to the friction coefficient of the coatings gradually decrease, and the wear failure mode changes from adhesive wear to abrasive wear.