Facile Route for Fabrication of Γ-Fe2o3@Ppy with Flower-Like Morphology from Iron Rust for High-Performing Asymmetric Supercapacitor

Suresh C. Pillai,Baolong Sun,Mengqi Yao,Yunjian Chen,Xianzhong Tang,Wencheng Hu

DOI: https://doi.org/10.2139/ssrn.4060460

2022-01-01

SSRN Electronic Journal

Abstract:The utilization of abundant scarp rust resources in nature is a remarkable research topic. Flower-like morphology of rust growing on the iron substrate by simulating corrosion in the marine atmosphere was obtained. A core-shell structure of γ-Fe 2 O 3 @PPy was developed through annealing and in situ chemical polymerization of pyrrole. As a supercapacitor anode, it exhibited a large areal capacitance of 2.202 F cm –2 at 1 mA cm –2 , which was found to be 2.5 times that of the original rust (0.878 F cm –2 ). And it achieved a capacity-retention rate of 90.7% after 8000 cycles. By matching with a cathode from nickel-cobalt layered double hydroxide (NiCoLDH) electrodeposited onto a porous Ni network, the device delivered the maximum areal capacitance of 1.263 F cm –2 , a high volumetric energy density of 7.9 mWh cm –3 at a power density of 14.99 mW cm –3 , and favorable cycle stability (capacitance retention of 90.1% after 8000 cycles). Most importantly, the energy storage mechanism of rust-based electrodes with flower-like structures was well discussed. This work achieved excellent capacitance performance of rust-based electrode materials and provided a new strategy for the direct application of naturally abundant rusted steel in supercapacitors.