Oxygen defect enriched hematite nanorods @ reduced graphene oxide core-sheath fiber for superior flexible asymmetric supercapacitor

Min Li,Zhengxin Luo,Jiaxin Quan,Ting Ding,Bilin Xu,Wanfei Li,Qinghui Mao,Wujun Ma,Hengxue Xiang,Meifang Zhu

DOI: https://doi.org/10.1016/j.jcis.2023.09.055

IF: 9.9

2023-09-14

Journal of Colloid and Interface Science

Abstract:The development of flexible asymmetric supercapacitors with high operating potential, superior energy density, and exceptional rate performance holds significant implications for the advancement of flexible electronics. Herein, oxygen-deficient hematite nanorods @ reduced graphene oxide (Fe 2 O 3−x @RGO) core-sheath fiber was rationally designed and fabricated. The introduction of oxygen defects can simultaneously enhance the conductivity , create a mesoporous crystalline structure, increase active surface area and sites. This leads to a significantly improved electrochemical performance, exhibiting a high specific capacitance of 525.2F cm −3 at 5 mV s −1 and remarkable rate capability (53.7 % retention from 5 to 100 mV s −1 ). Additionally, a flexible asymmetric supercapacitor was assembled employing Fe 2 O 3−x @RGO fibers as anode and MnO 2 /RGO fibers as cathode. This design achieved a maximum operating voltage of 2.35 V, high energy density of 71.4 mWh cm −3 , and outstanding cycling stability with 97.1 % retention after 5000 cycles. This study proposes a straightforward and efficient strategy to substantially enhance the electrochemical performances of transition metal oxide anodes, thereby promoting their practical application in asymmetric supercapacitors.

chemistry, physical