Abstract:In this study, a biobased phenolic adhesive was successfully developed by entirely substituting both petroleum-based phenol and formaldehyde with an unmodified corn stover biorefinery lignin and glyoxal (a biobased dialdehyde), respectively. Lignin-glyoxal resins were synthesized using an alkaline catalyst with a molar ratio of lignin to glyoxal of 1:2. Chemical, thermal, and mechanical properties of the lignin, lignin-based resins, and final adhesives were assessed following appropriate standard test methods. The analysis of lignins and lignin-based resin molar mass was performed using gel permeation chromatography. The lignin-glyoxal resin was found to have a 3-fold higher average molecular weight than the starting lignin, demonstrating the successful integration of lignin into the polymeric resin network. The curing of the formulated adhesives was studied using differential scanning calorimetry and dynamic mechanical analysis. Although the lignin-glyoxal resin had a higher curing temperature (167 °C) than a conventional phenol-formaldehyde resin (142 °C) and the formulated lignin-formaldehyde resin (146 °C), the rate and degree of cure were similar or better than the other two resins. The adhesion strengths of the formulated adhesives were determined using single-lap-joint veneer samples cured according to recommended press parameters for commercial adhesives. The lignin-glyoxal adhesive had a relatively high dry adhesion strength (3.9 MPa), with over 90% wood failure, but failed the wet adhesion test (boiling water test). Although the formulated lignin-glyoxal adhesive failed the boiling water test, it had excellent stability at room temperature water, remaining intact after 1 week during the water immersion test. The high dry adhesion strength makes this class of lignin-based formaldehyde-free adhesives a unique biobased glue for the production of interior grade plywood and oriented strand boards.A biobased adhesive was formulated by entirely replacing petroleum-based phenol and formaldehyde with lignin and glyoxal for interior plywood application.This article has not yet been cited by other publications.

Renewable Thiol–yne “click” Networks Based on Propargylated Lignin for Adhesive Resin Applications

Structure-property Relationships for Technical Lignins for the Production of Lignin-Phenol-formaldehyde Resins

Broad-spectrum lignin-based adhesives using thiol–silyl ether crosslinkers

Impact Of Lignin Source On The Performance Of Thermoset Resins

Preparation and properties of adhesives based on phenolic resin containing lignin micro and nanoparticles: A comparative study

A Review on Lignin‐Based Phenolic Resin Adhesive

Lignin-Glyoxal: A Fully Biobased Formaldehyde-Free Wood Adhesive for Interior Engineered Wood Products

Lignin Phenol Formaldehyde Resoles Using Base-Catalysed Depolymerized Kraft Lignin

Bio-Epoxy Resins Based on Lignin and Tannic Acids as Wood Adhesives—Characterization and Bonding Properties

A Novel Method of Self-Cross-Linking of Syringaldehyde with Activated Methoxy Groups via Cross-Coupling for Lignin-Based Wood Adhesives

Crosslinking reactions of a model aminated lignin compound as a platform for building thermosetting polymers for lignin-based bio adhesives

Improving the properties of phenol-lignin-glyoxal as a wood adhesive by lignin nanoparticles

Enzymatic Conversion of Lignosulfonate into Wood Adhesives: A Next Step towards Fully Biobased Composite Materials

Elucidating the Role of Lignin Type and Functionality in the Development of High-Performance Biobased Phenolic Thermoset Resins

Thermal and Gluing Properties of Phenol-Based Resin with Lignin for Potential Application in Structural Composites

Formaldehyde-free self-polymerization of lignin-derived monomers for synthesis of renewable phenolic resin

Kraft lignin-containing polyurethane adhesives: the role of hydroxypropylation on thermomechanical properties

Thermosetting Polymers from Lignin Model Compounds and Depolymerized Lignins

Fast Curing Bio-Based Phenolic Resins via Lignin Demethylated under Mild Reaction Condition

Epoxy resin synthesis using low molecular weight lignin separated from various lignocellulosic materials

Demethylation of Alkali Lignin with Halogen Acids and Its Application to Phenolic Resins