Abstract:With the increasing demand for high thrust-weight ratio aero-engines, the development of environmental barrier coatings (EBCs) for SiC-based ceramics is an enormous challenge, which requires both high temperature stability and resistance to molten calcium-magnesium-aluminosilicate (CMAS) corrosion. In this work, a novel high-entropy disilicate (Y0.25Yb0.25Er0.25Sc0.25)2Si2O7 ((4RE0.25)2Si2O7) EBC materials was prepared by a two-step process. The high-entropy disilicate powder was synthesized by sol-gel method, and then Y-Si-Al-O silicate glass was used as sintering aids to facilitate densification of the (4RE0.25)2Si2O7 ceramic by liquid sintering. The results of XRD, SEM and EDS showed that as-synthesized powders were pure high-entropy disilicate (4RE0.25)2Si2O7, and bulk (4RE0.25)2Si2O7 ceramic exhibited a dense structure, in which (4RE0.25)2Si2O7 grains were uniformly distributed into Y-Si-Al-O glass. Compared with single disilicate RE2Si2O7 (RE = Y and Er) ceramics, the high entropy (4RE0.25)2Si2O7 ceramic showed a good phase stability and almost no change in grain size during sintering at 1600 °C for in the holding time range of 5–15 h, suggesting a good high temperature stability. During molten CMAS corrosion, Ca2+ ions can diffuse into the Y-Si-Al-O glass phase wrapped on the surface of (4RE0.25)2Si2O7 grains, and then corrode (4RE0.25)2Si2O7 grains, thereby forming the corrosion zone consisting of reaction layer and diffusion layer. The Y-Si-Al-O glass can play a blocking layer role to suppress Ca2+ diffusion and mitigate molten CMAS corrosion, so that as-prepared (4RE0.25)2Si2O7 ceramic showed a relatively good ability for resisting molten CMAS corrosion. After molten CMAS corrosion at 1500 °C for 48 h, thickness of the reaction layer was only 73 µm. The results will be a solid foundation for the application of environmental barrier coating materials in long-period high temperature molten silicate environment.

Phase Composition and Property Evolution of (yb1−xhox)2si2o7 Solid Solution As Environmental/thermal Barrier Coating Candidates

Tunable properties of (Ho x Y 1-x ) 2 SiO 5 as damage self-monitoring environmental/thermal barrier coating candidates

(Ho0.25Lu0.25Yb0.25Eu0.25)2SiO5 high-entropy ceramic with low thermal conductivity, tunable thermal expansion coefficient, and excellent resistance to CMAS corrosion

Tunable properties of (HoxY1-x)2SiO5 as damage self-monitoring environmental/thermal barrier coating candidates

A high‐entropy (Er0.25Y0.25Ho0.25Yb0.25)2Si2O7 ceramic with good thermal properties and water‐vapor corrosion resistance

First-principles calculations and thermal-mechanical experimental studies on middle-entropy rare-earth disilicates

Preparation and water vapor corrosion behavior of high entropy rare earth disilicate (Y0.25Yb0.25Ho0.25Er0.25) 2Si2O7

High temperature corrosion behavior and the inhibition of apatite formation evolving from corrosion of (Y1−Yb )2SiO5 in water vapor environment

High-entropy (ho1/4er1/4dy1/4gd1/4)2 Si2O7: A Promising Thermal Environmental Barrier Coating Material

Effect of Heterogeneous Phases on Thermal-Mechanical Properties and CMAS Corrosion Resistance of (sc0.33er0.33yb0.34)2si2o7 Ceramics

High‐entropy (Ho1/4Er1/4Dy1/4Gd1/4)2Si2O7: A promising thermal environmental barrier coating material

Composition Effects on Elastic, Thermal and Corrosion Properties of Multiple-Re Silicate (ho1/4er1/4yb1/4lu1/4)2sio5 As a Promising Thermal and Environmental Barrier Coating Material

Enhanced High-Temperature Performance of Selected High-entropy Rare Earth Disilicates

Preparation and characterization of (Yb0.25Lu0.25Sc0.25Tm0.25)2Si2O7 as a potential environmental barrier coating

Preparation and corrosion resistance of high-entropy disilicate (Y0.25Yb0.25Er0.25Sc0.25)2Si2O7 ceramics

Thermal shock behavior and oxidation resistance of novel SiC nanowires+Si/Yb2Si2O7-Si/Yb2Si2O7 environmental barrier coatings

Synthesis and Thermal Conductivity of Ytterbium Silicate Doped with Sm and Gd for Environmental Barrier Coatings Application

Thermal durability of ytterbium silicate environmental barrier coating prepared by suspension plasma spray

High-temperature performance of thermal environmental barrier coatings in 90%H2O-10%O2 conditions at 1475 °C

Thermal properties and calcium-magnesium-alumino-silicate (CMAS) interaction of novel γ-phase ytterbium-doped yttrium disilicate (γ-Y1.5Yb0.5Si2O7) environmental barrier coating material

Equiatomic Quaternary (y1/4ho1/4er1/4yb1/4)(2)sio5 Silicate: A Perspective Multifunctional Thermal and Environmental Barrier Coating Material