Mesoscale pore structure of a high-performance concrete by coupling focused ion beam/scanning electron microscopy and small angle X-ray scattering

D. Troadec,Pierre,C. Davy,Levitz,S. Brisard,L. Michot

Abstract:This is the pre-peer reviewed version of the following article: “Mesoscale pore structure of a high ‐ performance concrete by coupling focused ion beam/scanning electron microscopy and small angle X ray scattering”, which has been published in final form at This article may be used for non-commercial purposes in accordance with Wiley Terms and Conditions for Use of Self-Archived Versions. See Wiley's Self-Archiving Policy. Abstract This contribution couples (1) Small Angle X-ray Scattering (SAXS) experiments of a High Performance Concrete (HPC) at the millimetric scale, and (2) Focused Ion Beam/Scanning Electron Microscopy (FIB/SEM) of the cement paste of the HPC, with 10-20 nm voxel size. The aim is to improve the understanding of the 3D pore network of the HPC at the mesoscale (tens of nm), which is relevant for fluid transport. The mature HPC is an industrial concrete, based on pure Portland CEMI cement, and planned for use as structural elements for deep underground nuclear waste storage. SAXS patterns are computed from the 3D pore images given by FIB/SEM (volumes of 61-118 µ m 3 ). They are positively correlated to SAXS measurements (volumes of 5 mm 3 ). Apart from correlations with FIB/SEM data, experimental SAXS allows to investigate a wider range of effects on the pore structure. These are mainly the HPC drying state, the presence of aggregates (by analyzing data on cement paste alone), and the use of PMMA resin impregnation.

Engineering,Materials Science,Physics