Abstract:Aramid nanofibers (ANFs) are self‐assembled into ANF films using a direct ink writing (DIW)‐based method in this work, which allows for controlled ANF alignment following the printing paths. The ANF films exhibit outstanding tensile modulus, strength and toughness in the alignment direction, and also inherit the high thermal stability of the aramid precursor. Aramid nanofibers (ANFs) are a strong and heat‐resistant nanomaterial that can be isolated from commercial para‐aramid fibers, which allow a bottom‐up self‐assembly to form ordered macroscale structures like ANF films. However, the anisotropic nature of high aspect ratio ANFs is not fully exploited when fabricating ANF films for the optimal mechanical properties. In this research, direct ink writing (DIW) is applied to produce ANF‐assembled films with arbitrary shapes, and the shear‐induced alignment of ANFs can follow the printing path direction. Therefore, controlled alignment of ANFs following the computer‐programmed printing pattern is achieved by DIW, which provides a path for the application of topology and nanofiber alignment optimization in nanofiber‐assembled films. In addition, the resulting DIW ANF films exhibit outstanding Young's modulus of 8.39 GPa, tensile strength of 198 MPa, and tensile toughness of 19.4 MJ m−3 in the alignment direction, together with a wide working temperature range up to 440 °C without losing 50% of its room temperature storage modulus. Moreover, the demonstrated self‐joining ability, rollability, and lamination processability of the DIW ANF films expand their potential applications toward high‐temperature ultrathin tubes, substrates for flexible printed circuit boards, and three‐dimensional all‐ANF lightweight structural parts in extreme environments.

Aqueous Dispersion of Aramid Nanofibers Achieved by Using Tannic Acid for Ultrahigh Strength Films

Functionalized Aramid Nanofibers Prepared by Polymerization Induced Self-Assembly for Simultaneously Reinforcing and Toughening of Epoxy and Carbon Fiber/epoxy Multiscale Composite

Dispersions of aramid nanofibers: a new nanoscale building block

Rapid and Scalable Synthesis of Novel Carboxylated Aramid Nanofibers for Simultaneously Improving the Strength and Toughness of Carbon Fiber/epoxy Laminates

Enhancement of Para-Aramid Fibers by Depositing Poly-P-paraphenylene Terephthalamide Oligomer Modified Multi-Walled Carbon Nanotubes

Metal ion-assisted fabrication of aramid nanofilm with high strength and toughness for the dye separation

Alignment Controlled Aramid Nanofiber‐Assembled Films

Timesaving, High-Efficiency Approaches to Fabricate Aramid Nanofibers

A Synergistic Interfacial and Topological Strategy for Reinforcing Aramid Nanofiber Films.

Efficient mechanochemically for the preparation of high performance aramid nanofibers and KOH/DMSO superbase

Preparation and Mechanical Properties of UV-Curable Epoxy Acrylate/Modified Aramid Nanofiber Nanocomposite Films

Preparation of aramid nanofiber and its application in polymer reinforcement: A review

Highly Intrinsic Thermal Conductivity of Aramid Nanofiber Films by Manipulating Intermolecular Hydrogen Bonding Interactions

A method for electrodepositing Aramid III nanofibers on copper electrodes

Large-area ultrastrong and stiff aramid nanofiber based layered nanocomposite films

Effects of aramid nanofibers on the mechanical properties of epoxy resin and improved adhesion with aramid fiber

Preparation and application of aramid nanofiber via carbodiimide assisted polymerization

Fabrication, Applications, and Prospects of Aramid Nanofiber

Fabricating the Strongest and Toughest Aramid Fibers by Small Addition of Carbon Nanotubes

Two-step re-protonation strategy to fabricate aramid nanofiber sheet (ANFS) based high performance composite film

Surface construction of ANF/CNT onto aramid fibers to enhance interfacial adhesion and provide real-time monitoring of deformation