Microstructural Evolution, Mechanical Behaviors and Strengthening Mechanism of 300 M Steel Subjected to Multi-Pass Laser Shock Peening

Hepeng Zhang,Zhongyi Cai,Jiaxuan Chi,Guofeng Han,Rujian Sun,Zhigang Che,Hongqiang Zhang,Wei Guo
DOI: https://doi.org/10.1016/j.optlastec.2021.107726
IF: 4.939
2021-01-01
Optics & Laser Technology
Abstract:300 M steel was treated by multi-pass laser shock peening (LSP). The microstructures were characterized by transmission electron microscopy (TEM), electron backscattered diffraction (EBSD) and X-ray diffraction (XRD). In addition, the surface roughness, microhardness, residual stress, impact toughness and mechanical properties after LSP were measured. The results showed that high-density dislocations were generated after multi-pass LSP and the dislocation motion dominated the deformation process. The intensity of texture decreased while low angle grain boundaries increased, and the grain refinement was not achieved after LSP. The residual stress transformed from tensile stress (+20 MPa) to compressive stress (-556 MPa) and the microhardness was 24.8% higher than the unpeened sample after LSP. Based on the linear superposition rule, a strengthening model was established to predict the contribution of dislocation and grain boundary strengthening on microhardness. Additionally, the fatigue life of peened samples increased by 165% compared with the unpeened ones. The improvement of high-cycle fatigue (HCF) properties was attributed to the rewarding compressive residual stress and microstructural evolution.
What problem does this paper attempt to address?