Abstract:The metallization reduction-magnetic separation process was adopted to carry out the experiments to promote the recovery ratio of valuable elements by adding diboron trioxide additive in this work. It is demonstrated that diboron trioxide has the function of destroying Si–O–Si bond for the reduction of ultra-high-titanium magnetite. The optimum experimental condition is found to be the reduction temperature of 1125 °C, the reduction time of 30min, and the diboron trioxide percent of 8 wt% for which the metallization ratio is 92%, and the recovery ratio of ferrum, vanadium, titanium is 90.9%, 78.5%, 76.1%, respectively. V and Ti are synchronously concentrated in non-magnetic materials. The phase composition transformation rule of the valuable components was Fe 3 O 4 (FeTiO 3 ) → FeO → Fe; FeTiO 3 (→ FeTi 2 O 5 ) → (Fe,Mg)Ti 2 O 5 ; FeTiO 3 → TiO 2 → Ti 3 O 5 → Ti 2 O 3 ; (Fe 3 O 4 + TiO 2 ) → Fe 3 Ti 3 O 10 → Fe. Increasing the temperature can promote the aggregation and growth of iron particles, but too high temperature is not conducive to the separation of Fe, V and Ti. It is evidently observed that when the temperature exceeds 1150 °C, the iron particles are closely connected with the gray titanium oxide, while at 1125 °C, the iron particles are relatively independent. Meanwhile, part of Ti is observed in silicate phase as solid-dissolved form because of high temperature and cause loss. Overall speaking, the metallization reduction-magnetic separation process with diboron trioxide as an additive has achieved the better separation of valuable components, with a higher degree of metallization, and large-scale lowered reaction temperature and time.

Beneficiation of Nb and Ti Carbides from Pyrochlore Ore Via Carbothermic Reduction Followed by Magnetic Separation

Enrichment of Nb and Ti from carbonatite pyrochlore ore via calcining-slaking followed by gravity separation

Experimental Investigation on Direct Reduction Followed by Magnetic Separation for Nb2O5-Bearing Ore

Enrichment of Rare Earth and Niobium from a REE-Nb-Fe Associated Ore via Reductive Roasting Followed by Magnetic Separation

Separation and Recovery of Iron and Nickel from Low-Grade Laterite Nickel Ore by Microwave Carbothermic Reduction Roasting

Study on Separation of Niobium and Iron from Low Grade Niobium Ore

Effects of Embedding Direct Reduction Followed by Magnetic Separation on Recovering Titanium and Iron of Beach Titanomagnetite Concentrate

Enrichment and Recovery Fe-containing Phases from High Iron Gibbsite Ore Based on Metallized Reduction and Magnetic Separation

Green and Efficient Utilization of Ferruginous Gibbsite Ore and Ferruginous Manganese Ore by Synergetic Carbothermic Co-Reduction–Magnetic Separation Process

Separation and recovery of valuable metals from low-grade REE–Nb–Fe ore

Synergetic Utilization of Zinc-Bearing Dust by Carbothermic Reduction-Roasting Process: Phase Transformation and Morphological Evolution

Study of Physicochemical Characteristics of Niobium-Containing Oxide Materials. Part 1. Thermodynamic Simulation

Beneficiation of Unwieldy Oolitic Hematite by Deep Reduction and Magnetic Separation Process

Thermodynamic Analysis and Experiment on the Conversion of Niobium Ferrite to Pyrochlore

Obtaining of niobium-containing ferroalloys from the Russian ore raw materials

The Phase Transformation of Baiyunebo Iron Ore Treated with Reductant Sintering

Carbothermal Reduction, Melting Separation, and Structural Analysis of Carbon-bearing Rare Earth Iron Ore Pellets

Extraction of Niobium from the Bayan Obo Tailings by “Flotation—Microwave Magnetic Roasting—Magnetic Separation”

A novel method of enhancing valuable element recovery for ultra-high-titanium magnetite