Fire-safe epoxy composite realized by MXenes based nanostructure with vertically arrayed MOFs derived from interfacial assembly strategy
Shui Yu,Chao Cheng,Keji Li,Junling Wang,Zhirong Wang,Haobo Zhou,Wei Wang,Yan Zhang,Yan Quan
DOI: https://doi.org/10.1016/j.cej.2023.143039
IF: 15.1
2023-04-21
Chemical Engineering Journal
Abstract:In this contribution, Ni-based metal organic frameworks (Ni-MOF) nanosheets with high specific surface area are grown on transition metals carbides (MXenes, denoted as MX) surface via vertical alignment, gestating the flame retardant of With the addition of 2.0 wt% , the peak heat release rate, peak smoke production rate, peak CO production rate, peak CO 2 production rate are reduced by 42.5 %, 26.7 %, 37.8 %, 54.9 %, while the peak concentrations of C 2 H 6 , CH 4 , HCN, NO, N 2 O are impaired by 91.3 %, 94.3 %, 89.6 %, 90.3 %, 60.9 %, suggesting the enhanced fire safety. Meantime, the fire performance index is elevated by 83.0 % and fire growth index is reduced by 37.2 %, demonstrating the promoted fire safety. Of note, the using of induces the promotion of 787.1 % in char yield after combustion, which shows higher graphitized degree and thus enables better protection for basal matrix. Flame retardation contrast with previous works also manifests the strength of in hindering the heat release and toxicants emission. This work offers a new paradigm for forging fire-safe polymer composites with low toxicity.
engineering, chemical, environmental