Abstract:The deterioration process and deterioration mechanism of magnesium oxychloride cement (MOC) in an alkaline environment were studied using a scanning electron microscope (SEM), an X-ray diffractometer (XRD), a Fourier transform infrared spectrometer (FT-IR) and a micro-electro-hydraulic servo pressure testing machine to investigate the effects of soaking time in 10 wt.% NaOH solution on the macro- and micro-morphology, phase composition and compressive strength of MOC samples. The results show that the deterioration of MOC samples under an alkaline environment is mainly caused by the alkaline environment providing more OH- ions, which can react with 5Mg(OH)2·MgCl2·8H2O (P 5) in the sample. The resulting reaction gives rise to a faster decomposition of 5Mg(OH)2·MgCl2·8H2O (P 5) and a substantial reduction in the strength of the sample, and finally leads to a gradual deterioration of MOC samples. Meanwhile, immersion time exhibits a significant effect on MOC samples. The extension of immersion time coincides with more OH- ions entering the sample, and the greater presence of OH ions increases the likelihood that more P 5 will produce a hydrolysis reaction, further resulting in the increased deterioration of the sample. After soaking for 6 h in alkaline media, the main phase composition of the surface layer of an MOC sample changes to MgO and Mg(OH)2, and its microscopic morphology is also dominated by round sheets, giving rise to a sharp decrease in its compressive strength (52.2%). When the immersion time is prolonged to 72 h, OH- ions have already immersed into the inner core of the sample, causing the disappearance of P 5 from the whole sample. At the same time, both the surface and inner core of the sample exhibit a disc-shaped morphology, and chalking phenomena also appear on the surface of the sample. This reduces the compressive strength of the sample to 13.5 MPa, only 20% of its compressive strength in water. The compressive strength of the sample after 120 h of immersion is as low as 8.6 MPa, which is lower than that of the sample dipped in water for 21 days (9.5 MPa). As a result, the MOC samples studied in alkaline environments exhibit a faster deterioration rate, mainly because of a faster hydrolysis reaction by P 5, caused by more OH- ions.

A study on the salt attack performance of magnesium oxychloride cement in different salt environments

Study on dynamic compression properties of ultra-high toughness cementitous composites under cyclic wetting and drying of salt spray

Research and Engineering Application of Salt Erosion Resistance of Magnesium Oxychloride Cement Concrete

Effect of modified supplementary cementitious material on performance of mortar and concrete in marine environment

Degradation Mechanisms of Chloride Contaminated Cast-in-Situ Concrete Partially Exposed to Magnesium-Sulfate Combined Environment

Meso-scale Mechanical Deterioration of Mortar Due to Sodium Chloride Attack

Study on Bonding Performance of Magnesium Phosphate Cement Mortar in Chloride Corrosion Environment

Degradation characteristics of Portland cement mortar incorporating supplementary cementitious materials under multi-ions attacks and drying-wetting cycles

Preparation of Low-Cost Magnesium Oxychloride Cement Using Magnesium Residue Byproducts from the Production of Lithium Carbonate from Salt Lakes

Study on the Stability of Low-Carbon Magnesium Cementitious Materials in Sulfate Erosion Environments

Mechanical Performance and Chloride Penetration of Calcium Sulfoaluminate Concrete in Marine Tidal Zone

Research on Deterioration Behavior of Magnesium Oxychloride Cement Under High Humidity and High Temperature

Chloride-induced Corrosion Patterns of Reinforcements in Simulated Pore Solutions of Calcium Sulfoaluminate Cement Concrete: an Analytical Study

Effects of Cyclic Seawater Exposure on the Mechanical Performance and Chloride Penetration of Calcium Sulfoaluminate Concrete

Effect of Chlorine Salt on Durability of Mineral Admixture Concrete under Different Conditions

Study on the Deterioration Mechanism of Magnesium Oxychloride Cement under an Alkaline Environment

Chloride Ingress Profiles and Binding Capacity of Mortar in Cyclic Drying-Wetting Salt Fog Environments

Degradation mechanism of cement mortar exposed to combined sulfate–chloride attack under cyclic wetting–drying condition

Experimental evaluation of salt corrosion resistance of potassium salt magnesium phosphate cement coating slurry

Strength and Leaching Characteristics of Magnesium Phosphate Cement-Solidified Zinc- Contaminated Soil under the Effect of Acid Rain

Degradation progress of Portland cement mortar under the coupled effects of multiple corrosive ions and drying-wetting cycles