Bioactive Microarc Oxidized TiO2-based Coatings for Biomedical Implication
Daqing Wei,Yu Zhou
DOI: https://doi.org/10.5772/14169
2011-01-01
Abstract:To prepare the bioactive coatings on titanium and its alloys, introductions of Ca and P elements into MAO were taken into account.In previous studies, various calcium salts such as calcium acetate,glycerophosphate disodium salt pentahydrate, calcium glycerophosphate and calcium dihydrogen phosphate were used in MAO process.In the previous research, titania-based coatings on titanium were prepared by MAO at various applied voltages (250-500V) in an electrolytic solution containing glycerophosphate disodium salt pentahydrate and calcium acetate monohydrate (Song et al. 2004).Ca-and P-containing titania-based coatings were formed on the titanium substrates.The phase, Ca and P content, morphology and thickness of the coatings were strongly dependent on the applied voltage.In particular, Ca-and P-containing compounds such as CaTiO 3 , Ca 2 P 2 O 7 and Ca 3 (PO 4 ) 2 were produced at higher voltages (>450 V).Besides theglycerophosphate disodium salt pentahydrate, calcium glycerophosphate was also used.In the electrolyte of calcium glycerophosphate and calcium acetate, the titanium anodic oxide coating is porous, highly crystalline, and rich in Ca and P. The optimum condition is that the concentration of the electrolyte is 0.02M calcium glycerophosphate and 0.15M calcium acetate, and current density and final voltage are 70 A/m 2 and 350 V, respectively (Zhu et al., 2001).To achieve high amounts of Ca, researchers (Frauchiger et al., 2004) used a new electrolyte containing Ca-EDTA chelate complex to prepare MAO coating.Based on the previous researches, authors have developed the MAO coatings only containing P. The MAO coating formed at 300 and 350 V after oxidizing for 5 min show good surface properties.In addition, as mentioned above, to achieve high amounts of Ca, EDTA was used to add into the electrolyte.Authors further investigated the effects of applied voltage and electrolyte composition and concentrations on the structures of the MAO coatings (e.g., phase composition, surface morphology, micropore number and size, element distribution on the surface and cross-sectional characters, etc) (Wei b et al., 2007).In the MAO coating formed on Ti6Al4V, TiO 2 nanocrystals were randomly distributed in Ca-and P-doped matrix, and their crystal size was 30-40 nm.With increasing the applied voltage, the surface toughness, micropores size, Ca and P concentrations, coating thickness are increased.High applied voltage promoted the formation of rutile.However, besides the TiO 2 and amorphous phase were observed, no other phase were detected at different applied voltages, not similar the previous researches.In this electrolyte, the EDTA impeded the crystallization of TiO 2 crystals during the MAO process.Besides the above electrolyte, the similar electrolyte with addition of HA was also investigated.It was found that the addition of HA promoted the formation of anatase (Wei c et al., 2007).Recently, bioactive glass components (BGC) doped MAO coatings on titanium were noticed by authors.This electrolyte was composed of Ca(CH 3 COO) 2 •H 2 O, Na 2 SiO 3 , EDTA-2Na and NaOH.And the results indicated that the surface morphology, phase composition and elemental concentrations are highly depended on the applied voltages.And BGC doped TiO 2 -based coatings exhibit good interface bonding with titanium, showing a graded www.intechopen.comBioactive Microarc Oxidized TiO 2 -based Coatings for Biomedical Implication 203 structure in elemental concentrations of Si, Ca, Na, O, Ti, etc..Moreover, these elements were distributed uniformly on the surface of BGC doped TiO 2 -based coatings.During the MAO treatment process, Ti could not be oxidized sufficiently, thus the TiO phase was also formed according to XPS resutls.Based on the above researches, generally speaking, the structures such as phase composition, surface morphology and elemental composition of the MAO coatings are highly dependent on the MAO process parameters such as the applied voltage, oxidizing time, frequency, duty cycle and electrolyte composition, etc., especially the applied voltage and electrolyte composition.