Effects of deformation temperatures on microstructures, aging behaviors and mechanical properties of Mg-Gd-Er-Zr alloys fabricated by hard-plate rolling
Ke Liu,Dalong Hu,Feng Lou,Zijian Yu,Shubo Li,Xian Du,Wenbo Du
DOI: https://doi.org/10.1016/j.jma.2022.10.009
IF: 11.813
2022-11-21
Journal of Magnesium and Alloys
Abstract:Highlights • The high rolling temperature would impede the DRX occurrence for these final-rolled sheets. • The reduction of the volume fraction of this β phases led to the highest peak-aging hardness in R-450 °C sheet. • The precipitate chains in R-385 °C + A sheets were beneficial for strength and elongation. • The traditional precipitation characteristic in R-450 °C + A sheet was bad for elongation but good for strength. • The peak-aging R-450 °C sheet showed the highest strength, i.e. UTS of 518±17 MPa and YS of 438±18 MPa. In this investigation, a high-strength Mg-12Gd-1.0Er-0.5Zr (wt.%) alloy sheet was produced by hot extrusion (HE) and subsequent hard-plate rolling (HPR) at different temperatures. The results indicate that the microstructures of these final-rolled sheets are inhomogeneous, mainly including coarse deformed grains and dynamic recrystallized (DRXed) grains, and the volume fraction of these coarse deformed grains increases as the rolling temperature increases. Thus, more DRXed grains can be found in R-385 °C sheet, resulting in a smaller average grain size and weaker basal texture, while the biggest grains and the highest strong basal texture are present in R-450 °C sheet. Amounts of dynamic precipitation of β phases which are mainly determined by the rolling temperature are present in these sheets, and its precipitation can consume the content of Gd solutes in the matrix. As a result, the lowest number density of β phase in R-450 °C sheet is beneficial to modify the age hardening response. Thus, the R-450 °C sheet displays the best age hardening response because of a severe traditional precipitation of β' (more) and β Η / β Μ (less) precipitates, resulting in a sharp improvement in strength, i.e. ultimate tensile strength (UTS) of ∼ 518 ± 17 MPa and yield strength (YS) of ∼ 438±18 MPa. However, the elongation (EL) of this sheet reduces greatly, and its value is ∼ 2.7 ± 0.3%. By contrasting, the EL of the peak-aging R-385 °C sheet keeps better, changing from ∼ 4.9 ± 1.2% to ∼ 4.8 ± 1.4% due to a novel dislocation-induced chain-like precipitate which is helpful to keep good balance between strength and ductility.
metallurgy & metallurgical engineering