Structure refinement, defects evolution and calcium doping of Sr2CeO4 microwave dielectric ceramics with high quality factor
Ao Zhang,Huiqing Fan,Dingwei Hou,Fan Yang,Yanqin Chen,Weijia Wang,Wenqiang Dong
DOI: https://doi.org/10.1016/j.ceramint.2022.05.303
IF: 5.532
2022-09-15
Ceramics International
Abstract:Sr2-2xCa2xCeO4 (x = 0, 0.025, 0.05, 0.1, 0.2, 0.4, 0.6, 0.8) ceramics were synthesized through cold isostatic pressing and solid-state reaction. The microstructure, defects, microwave dielectric properties, and the effect of Ca2+ doping of Sr2CeO4 ceramics were systematically investigated. As the sintering temperature increased, the densities of Sr2CeO4 ceramics rose, the content of oxygen vacancies increased, and Ce4+ reduction would be enhanced. In addition, the Sr2CeO4 structure had poor compatibility with Ca2+. The major phase could be kept unchanged only when x ≤ 0.1. The reason was that the doping of Ca2+ intensified the distortion of the CeO6 octahedron and induced the structural transformation of the common edges (Sr2CeO4) to the common angles (SrCeO3). With the increase of dopant, the densities of Sr2-2xCa2xCeO4 ceramics increased significantly, while the content of oxygen vacancies also increased. The microwave dielectric properties were mainly influenced by the density, structural symmetry, defects, and the second phase SrCeO3. The dielectric permittivity (εr) of 13.4–15, the quality factor (Qf) of 118,580–52,170 GHz, and the temperature coefficient of resonant frequency (τf) of −58.3 ∼ −47.5 ppm/°C were obtained for Sr2-2xCa2xCeO4 ceramics When x ≤ 0.1. This work has provided a foundation for further research on cerate microwave dielectric ceramics.
materials science, ceramics