Dual-tuning of de/hydrogenation kinetic properties of Mg-based hydrogen storage alloy by building a Ni-/Co-multi-platform collaborative system
Hui Yong,Shuai Wang,Jiangwei Ma,Kewei Zhang,Dongliang Zhao,Jifan Hu,Yanghuan Zhang
DOI: https://doi.org/10.1016/j.ijhydene.2021.04.198
IF: 7.2
2021-07-01
International Journal of Hydrogen Energy
Abstract:<p>The Mg-based hydrogen storage alloy with multiple platforms is successfully prepared by ball milling Co powder and Mg-RE-Ni precursor alloy, and its hydrogen storage behavior was investigated in detail by XRD, EDS, TEM, PCI, and DSC methods. The ball-milled alloy consists of the main phase Mg, the catalytic phases Mg<sub>2</sub>Ni, Mg<sub>2</sub>Co as well as a small amount of Mg<sub>12</sub>Ce, and convert into the MgH<sub>2</sub>–CeH<sub>2.73</sub>-Mg<sub>2</sub>NiH<sub>4</sub>–Mg<sub>2</sub>CoH<sub>5</sub> composite after hydrogenation. The composite has three PCI platforms corresponding to the reversible de/hydrogenation reaction of Mg/MgH<sub>2</sub>, Mg<sub>2</sub>Ni/Mg<sub>2</sub>NiH<sub>4</sub> and Mg<sub>6</sub>Co<sub>2</sub>H<sub>11</sub>/Mg<sub>2</sub>CoH<sub>5</sub>. Among them, the transformation between Mg<sub>2</sub>Ni and Mg<sub>2</sub>NiH<sub>4</sub> triggers the "spill-over" effect which promote the decomposition of MgH<sub>2</sub> phases and enhances the hydrogen desorption kinetics. Meanwhile, the conversion of the Mg<sub>6</sub>Co<sub>2</sub>H<sub>11</sub> to Mg<sub>2</sub>CoH<sub>5</sub> phase induces the "chain reaction" effect, which leads to preferential nucleation of Mg phase and improves the hydrogen absorption kinetics. Therefore, the Mg-RE-Ni-Co alloy has a double improvement on hydrogen absorption and desorption kinetics. Concretely, the alloy has an optimal hydrogen absorption temperature of 200 °C, at which it can absorb 5.5 wt. % H<sub>2</sub> within 40 s. Under the conditions, the capacity of absorption almost reaches the maximum reversible value (about 5.6 wt. %). Besides, the alloy has a dehydrogenation activation energy of 67.9 kJ/mol and can desorb 5.0 wt. % H<sub>2</sub> within 60 min at the temperature of 260 °C.</p>
energy & fuels,electrochemistry,chemistry, physical