Abstract:Because of its extreme hardness, wear resistance, good thermal conductivity and low thermal expansion coefficients, a diamond tool exhibits a range of properties which makes it a key and unique component in many fields of mechanical engineering. In comparison with the other types of diamond tools, the thin film diamond-coated cutting inserts have great potentialities in the commercial application because of its low costs for fabrication equipment and high performance. Thus, they are on the verge of becoming the next generation of tools used for high speed machining non-ferrous metals and alloys, metal-compound materials, and hard brittle non-metals. However, the poor adhesion of the diamond film on the substrate becomes the main technical barriers for the successful development and commercialization of diamond-coated tools. In this paper, diamond thin films were deposited on WC-Co cemented carbide substrates by the electron aided hot filament chemical vapor deposition (EACVD), using a mixture of hydrogen and acetone as source gases. A new multiple chemical pre-treatment including microwave oxidation, reaction in alkaline solution and cleaning by ultrasonic treatment in acid solution has been performed for free shape cemented WC-Co drills in order to increase the diamond nucleation and to enhance the coating adhesion. And also, another new pretreatment method using Ar-HZ gas etching decarburization by microwave plasma is performed for the WC-Co substrate surface. The influences of this pretreatment technique on the adhesion strength, diamond nucleation and surface morphology of the diamond thin film are investigated. Scanning electron microscope (SEM) was used to view the substrate morphology, and to examine the cobalt removal. After pre-treatment, the surface of the WC-Co substrate becomes slightly rough, but its composition and structure shows no changes identified by X-ray diffraction (XRD). Scanning electron microscope (SEM) indicates a distribution of uniform micro-roughness WC grains on substrate surface. And also the research results show that the pretreatment using Ar-H etching decarburization by microwave plasma is an effective method to enhance adhesive strength. The appropriate CVD processes were studied for the fabrication of tools with complex geometries. An adequate amount of additive can effectively prevent the overflow of Co from inner to surface of the substrate and avoid the catalytic effect of Co during CVD. The smooth diamond film with low surface roughness can be deposited by increasing the carbon source concentration and reducing the reactive pressure at the later stage of CVD process. The diamond morphology quality and homogeneity of coatings were characterized by SEM and Raman spectroscopy. The cutting performances of diamond-coated tools were studied by the cutting tests of difficult-to-machine materials. The research results show that the high quality diamond coating has been deposited on complex shape substrates for WC-Co cemented carbide twist drills. The cutting performances of diamond-coated drills are improved further by the new pretreatment and CVD process. It is of great significance for the fabrication and application of the diamond-coated tools with complex geometries.

Enhanced Adhesive Strength of Diamond Coated on Polycrystalline Diamond Substrate by Optimized Substrate Component

Improvement Of Adhesive Strength And Surface Roughness Of Diamond Films On Co-Cemented Tungsten Carbide Tools

Study on deposition and characterization of diamond coated cylinder-shaped substrate

Research Progress on Cutting Tools Made from WC?Co Cemented Carbide Substrates and Coated with CVD Diamond

Improvement of Film-to-Substrate Adhesion for Diamond and Related Films by Plasma-Based Technologies

A New Multiple Chemical Pretreatment For Fabrication Of High Quality Cvd Diamond-Coated Drills

Study On The Properties Of Diamond Films On Cemented Carbide Substrates By Surface Implantation Pretreatment Process

Effect of Pretreatment Strategy on the Microstructure, Mechanical Properties and Cutting Performance of Diamond Coated Hardmetal Tools Using HFCVD Method

Effect of Microwave Plasma-etching Decarburization upon Adhesive Strength of CVD Diamond Film to WC - Co Substrate

Effects of Chemical Surface Pretreatments on Diamond Coatings on Cemented Tungsten Carbide Substrate

Improvement of Adhesive Strength and Surface Roughness of Diamond-Coated Thin Film Tools

Fabrication and application of high quality diamond-coated tools

Preparation, wear resistance, and impact toughness of homoepitaxial diamond film deposited on polycrystalline diamond compact by HFCVD method

Studies of Adhesion and Roughness of Diamond Coated Drills and Influence on Cutting Performance

Sandblasting Pretreatment for Deposition of Diamond Films on Wc-Co Hard Metal Substrates

Reprint of “A Study of CVD Diamond Deposition on Cemented Carbide Ball-End Milling Tools with High Cobalt Content Using Amorphous Ceramic Interlayers”

Improvement in the universality of high-performance CVD diamond coatings on different WC-Co substrates by introducing multilayered diamond/β-SiC composite

A new pretreatment method for WC-Co substrate for CVD deposition

Uniform diamond coatings on WC-Co hard alloy cutting inserts deposited by a microwave plasma CVD

Improved adhesion of diamond coating on cobalt-cemented tungsten carbide hardmetal by using pulsed-UV-laser substrate surface pretreatment

Interface characteristics of CVD diamond coating on WC-Co cemented carbide substrate