Abstract:The tension-compression yield asymmetry caused by the strengthening of Mg-Zn-Gd-Zr alloy due to extrusion deformation is an important issue that must be addressed in its application. In this study, the effects of loading direction on the tensile and compressive mechanical behaviors of Mg-5Zn-2Gd-0.2Zr alloy were systematically investigated. As the loading angle (the angle between the loading direction and the extrusion direction) increases from 0° to 30°, 45°, 60° and 90°, the tensile yield strength decreases more significantly than the compressive yield strength. Consequently, the tension-compression yield asymmetry is gradually improved. Additionally, the ultimate compressive strength decreases more markedly than the ultimate tensile strength with the increment of the loading angle. In tensile tests conducted at 0°, 30° and 45°, two distinct stages of decreasing strain hardening rates are typically observed. For the 60° and 90° tensile tests, one unusual ascending stage of strain hardening rate is observed. For all compressive tests, three stages of strain hardening are consistently noted; however, the increment in strain hardening rate caused by {10–12} extension twinning decreases with the increasing loading angle. A model combining loading angle and Schmid factor distribution was established. The calculated results indicate that the dominant deformation modes during the yielding process also vary significantly with the loading conditions. This clarification highlights the differences in yield strength variations between tension and compression. Finally, an analysis of the plane trace and crack propagation direction near the fracture surface reveals the fracture mechanisms associated with tensile and compressive tests at different loading directions. This study promotes understanding of the mechanical behaviors of Mg-5Zn-2Gd-0.2Zr alloy under different loading directions, and helps to thoroughly elucidate the anisotropic effects of texture on the mechanical properties of magnesium alloys.

Tension-Compression Asymmetric Twinning Behavior in a Cast Mg-Gd-Y-Zr Alloy

Tension-compression asymmetry of temperature dependencies in Mg rare-earth alloys

Influence of precipitation on tension and compression twinning in Mg-6.5Zn alloy

Twin recrystallization mechanisms in a high strain rate compressed Mg-Zn alloy

Effect of twinning on the deformation behavior of an extruded Mg-Zn-Zr alloy during hot compression testing

Effect of Loading Direction on Tensile-Compressive Mechanical Behaviors of Mg-5Zn-2Gd-0.2Zr Alloy with Heterogeneous Grains

Effects of extrusion ratio and subsequent heat treatment on the tension-compression yield asymmetry of Mg-4.58Zn-2.6Gd-0.18Zr alloys

Compressive stress and shear stress on the deformation mechanism of Mg-13Gd-4Y–2Zn-0.5Zr alloy at different deformation temperatures

A Study of {10-12} Twinning Activity Associated with Stress State in Mg-3Al-1Zn Alloy during Compression

The Microstructure and Mechanical Properties of As-cast Mg-10Gd-3Y-xZn-0.6Zr (x=0, 0.5, 1 and 2 Wt%) Alloys

Hot compression behavior and microstructure evolution of Mg-Gd-Y-Zn-Zr alloy

Flow softening and dynamic recrystallization behavior of a Mg-Gd-Y-Nd-Zr alloy under elevated temperature compressions

Improvement of dynamic compression properties and strengthening mechanism of Mg–Y–Nd–Gd–Zr alloy by pre-twinning

Deformation mechanism of fine grained Mg–7Gd–5Y–1.2Nd–0.5Zr alloy under high temperature and high strain rates

Twinning Behavior, Microstructure Evolution and Mechanical Property of Random-Orientated ZK60 Mg Alloy Compressed at Room Temperature

Effects of trace Zn on the deformation mechanisms of Mg‐Gd‐Y‐Zr alloy investigated by in‐situ synchrotron diffraction

Strength Differential Effect and Anisotropy of Mg–1.9Mn–0.3Ce (Wt-%) Alloy Subjected to High-Rate Loadings

Twinning–Detwinning-Dominated Cyclic Deformation Behavior of a High-Strength Mg-Al-Sn-Zn Alloy during Loading Reversals: Experiment and Modeling

Deformation Mechanism, Microstructure, and Mechanical Properties Evolution of Mg–Gd–Y–Zr Alloy during Cold Torsion

Microstructure Evolution and Selection Behavior of Twin Variants of Mg-5Gd-3Y-0.5Zr Alloy during Secondary Deformation

Quantitative investigation on the {10–12} twinning-detwinning behavior and twinning transfer of an extruded Mg-2.8Y sheet during compression-tension loading via quasi-in-situ EBSD observation