Influences of Inert Particles on Corrosion Behavior of Carbon Steel under Sodium Chloride Droplet

Yanhua Wang,Lian Zhong
DOI: https://doi.org/10.1149/ma2016-02/9/1124
2016-01-01
ECS Meeting Abstracts
Abstract:In ambient atmosphere, the surface of structural materials are usually covered by a layer of solid matter, containing soluble species and inert particles. The soluble species are highly hygroscopic and corrosive to steel, the inert particles can also affect corrosion by changing the mass transfer process. In this paper, the influence of inert particles on the droplet corrosion of carbon steel was studied by using the array electrode technique, potentiodynamic polarization technique and the electrochemical impedance spectroscopy. The current map exhibited the typical Evans distributions, with the anodes at the centre and the cathodes at the peripheral, which was not affected by the deposition of the inert particles. However, the spreadability of droplets increased with the increase of the amount of inert particles, which resulted in the expansion of corrosion activity area. In addition, the impedance spectra showed two capacitive loops with the deposition of inert particles, and the capacitive loop in the high frequencies was attributed to the blocking effect of the inert particles. The corrosion behavior of carbon steel was affected by these two aspects, the spreadability of droplets and the blocking effect of the inert particles. With the increase of the amount of particles, the average current value decreased firstly and then increased. There was a critical value in the deposition amount of the inert particles. When the amount was lower than the critical value, it could hinder corrosion. While, when the amount was higher than the critical value, it would accelerate corrosion owing to the expansion of droplets. The underlying mechanism was analyzed and a model was proposed. Figure 1
What problem does this paper attempt to address?