Abstract:Pitting and localized corrosion of carbon steel is considered to be a complex process influenced by a wide range of parameters such as temperature, bulk solution pH, and chloride ion concentration. Solution pH is known to influence corrosion product characteristics and morphology in CO2- and H2S-containing corrosion systems. However, from the perspective of pitting corrosion in CO2-saturated environments, the extent to which bulk pH of solutions and the presence of corrosion products influence localized attack is still not clearly understood. This paper presents an investigation into the role of pH on the characteristics of corrosion product and pitting corrosion behavior of X65 carbon steel (UNS K03014) in CO2-saturated brine. Pitting corrosion studies were conducted over 168 h at 50°C in 3.5 wt% NaCl solutions at different bulk pH (buffered to pH values of 6.6 and 7.5 in some cases) in order to understand and correlate the role of pH on corrosion product morphology, chemistry, initiation, and propagation of pits within each distinct environment. Corrosion product composition and morphology are identified through a combination of electrochemical and surface analysis techniques, which include scanning electron microscopy and x-ray diffraction. The extent of corrosion damage of the carbon steel is evaluated through the implementation of surface interferometry to study discrete pit geometry, namely the size, depth, and aspect ratio. Results indicate that the process of pit initiation and propagation of carbon steel in CO2 corrosion environment is different depending upon bulk solution pH. At low pH (pH values starting at 3.8), pitting initiates faster and propagates steadily along with significant uniform corrosion resulting from the formation of an “amorphous” form of FeCO3. At higher pH, uniform corrosion is significant, while pitting initiates with increasing protection from crystalline FeCO3. At a pH value of 7.5, pitting corrosion initiation occurs after and/or during pseudo-passivation is achieved as a result of the formation of a “protective and pseudo-passivating” FeCO3 film.

Influence of Soil Particle Size, Covering Thickness, and pH on Soil Corrosion of Carbon Steel

Effect of particle size on the electrochemical corrosion behavior of X70 pipeline steel

The Influence of pH on Localized Corrosion Behavior of X65 Carbon Steel in CO2-Saturated Brines

Investigation of Microstructure and Corrosion Behavior of Weathering Steel in Aqueous Solution Containing Different Anions for Simulating Service Environments

Effects of chloride ions on corrosion of ductile iron and carbon steel in soil environments

Investigation on the initial atmospheric corrosion of mild steel in a simulated environment of industrial coastland by thin electrical resistance and electrochemical sensors

Corrosion of Steel Fibers in Chloride-Contaminated Simulated Concrete Pore Solutions

Effect of SO42− in aerobic/anaerobic environment and its interaction with HCO3− on corrosion behavior of carbon steel

Coupling Effects of pH and Dissolved Oxygen on the Corrosion Behavior and Mechanism of X80 Steel in Acidic Soil Simulated Solution

ENVIRONMENTAL FACTORS CONTROLLING EARLY CORROSION PERFORMANCE OF CARBON STEEL UNDER LIQUID LAYER CONTAINING SO42

Understanding the interaction between erosion and corrosion of pipeline steel in acid solution of different pH

Effect of Electric Fields on the Initial Corrosion Behaviour of Carbon Steel at Different Chloride Salt Concentrations

CO2 Corrosion of Low Carbon Steel Under the Joint Effects of Time-Temperature-Salt Concentration

Application of Electrochemical Impedance Spectroscopy to Evaluate the Corrosion Behavior of 2304 Duplex Stainless Steel Reinforced Rebar in Concrete Exposed in Chloride-Rich Environment

Interaction of silty sand and preformed corrosion products on N80 carbon steel in CO2 environment

Investigation of Q235 steel electrochemical corrosion behavior in naturally dried sandy soil

Study of Overprotective-Polarization of Steel Subjected to Cathodic Protection in Unsaturated Soil

Influence of the Dissolved Oxygen Concentration in Artificial Seawater on the Corrosion Behavior of Q235 Mild Steel

Influence of Direct Current Electric Field on the Formation, Composition and Microstructure of Corrosion Products Formed on the Steel in Simulated Marine Atmospheric Environment

Atmospheric Corrosion of Steel A3 Deposited with Ammonium Sulfate and in the Presence of Sulfur Dioxide

Sodium silicate corrosion inhibition behaviour for carbon steel in a dynamic salt water environment