Speed dependence of liquid superlubricity stability with H<sub>3</sub>PO<sub>4</sub> solution

Chen Xiao,Jinjin Li,Lei Chen,Chenhui Zhang,Ningning Zhou,Linmao Qian,Jianbin Luo

DOI: https://doi.org/10.1039/c7ra09217b

2017-01-01

RSC Adv.

Abstract:The water-based superlubricity can be promoted to a high-speed of 1.6 m s−1 after pre-running-in at low-speed of 0.075 m s−1.

What problem does this paper attempt to address?

Speed Dependence of Liquid Superlubricity Stability with H3PO4 Solution

Chen Xiao,Jinjin Li,Lei Chen,Chenhui Zhang,Ningning Zhou,Linmao Qian,Jianbin Luo

DOI: https://doi.org/10.1039/c7ra09217b

IF: 4.036

2017-01-01

RSC Advances

Abstract:The water-based superlubricity can be promoted to a high-speed of 1.6 m s−1 after pre-running-in at low-speed of 0.075 m s−1.
Investigation of Superlubricity Achieved by Polyalkylene Glycol Aqueous Solutions

Hongdong Wang,Yuhong Liu,Jinjin Li,Jianbin Luo

DOI: https://doi.org/10.1002/admi.201600531

IF: 5.4

2016-01-01

Advanced Materials Interfaces

Abstract:Ultralow friction coefficient (μ) of a polyalkylene glycol (PAG) aqueous solution obtained in both droplet state (40 μL) and full immersion state after a running‐in period. Here, two key factors in achieving the superlubricity state (μ < 0.01) demonstrated: the low shearing strength of the hydrated layer and the presence of a suitable amount of free water molecules. In the initial running‐in period, a decrease in contact pressure contributes to the formation of elastohydrodynamic behavior of fluid. The hydrogen‐bonded PAG chains produce a hydrated layer between two sliding solid surfaces so as to lower the shear strength. The presence of free water molecules effectively weakens interactions between polymer chains. Therefore, the superlubricity state can be realized over a wide range of concentrations (30–60 wt%). Present work shows the mechanism of a stable lubricating system with superior tribological properties, and has a significant potential in industrial applications.
Temporary or Permanent Liquid Superlubricity Failure Depending on Shear-Induced Evolution of Surface Topography

Yuanyuan Jiang,Chen Xiao,Lei Chen,Jinjin Li,Chenhui Zhang,Ningning Zhou,Linmao Qian,Jianbin Luo

DOI: https://doi.org/10.1016/j.triboint.2021.107076

IF: 5.62

2021-01-01

Tribology International

Abstract:The sensitivities to operation conditions may reduce the reliability and stability of liquid superlubricity and limit industrial application of the lubrication system. Here, we demonstrated that the superlubricity of Si3N4/glass sliding interface lubricated with H3PO4 solution degenerated as speed/load decreased or increased, which was temporary or permanent depending on the different shear-induced evolutions of substrate surface topographies. The smooth contacting surface produced in superlubricity stage could be maintained during the temporary superlubricity failure at decreased speed/load condition and the superlubricity was restored when speed/load was recovered. Differently, severe wear induced by high load/speed disabled the hydration lubricating layer and resulted in irreversible superlubricity degeneration. Finally, the relationship between the lubrication state of liquid superlubricity system and the sliding surface roughness was established.
Achieving macroscale superlubricity with ultra-short running-in period by using polyethylene glycol-tannic acid complex green lubricant

Changhe Du,Tongtong Yu,Zishuai Wu,Liqiang Zhang,Ruilin Shen,Xiaojuan Li,Min Feng,Yange Feng,Daoai Wang

DOI: https://doi.org/10.1007/s40544-022-0660-3

IF: 4.924

2023-01-07

Friction

Abstract:Superlubricating materials can greatly reduce the energy consumed and economic losses by unnecessary friction. However, a long pre-running-in period is indispensable for achieving superlubricity; this leads to severe wear on the surface of friction pairs and has become one of the important factors in the wear of superlubricating materials. In this study, a polyethylene glycol-tannic acid complex green liquid lubricant (PEG10000-TA) was designed to achieve macroscale superlubricity with an ultrashort running-in period of 9 s under a contact pressure of up to 410 MPa, and the wear rate was only 1.19 × 10 −8 mm 3 ·N −1 ·m −1 . This is the shortest running-in time required to achieve superlubricity in Si 3 N 4 /glass (SiO 2 ). The results show that the strong hydrogen bonds between PEG and TA molecules can significantly reduce the time required for the tribochemical reaction, allowing the lubricating material to reach the state of superlubrication rapidly. Furthermore, the strong hydrogen bond can share a large load while fixing free water molecules in the contact zone to reduce shear interaction. These findings will help advance the use of liquid superlubricity technology in industrial and biomedical.

engineering, mechanical
Water-based Superlubricity in Vacuum

Chen Xiao,Jinjin Li,Lei Chen,Chenhui Zhang,Ningning Zhou,Tao Qing,Linmao Qian,Jiyang Zhang,Jianbin Luo

DOI: https://doi.org/10.1007/s40544-018-0212-z

IF: 4.924

2018-01-01

Friction

Abstract:This study achieved water-based superlubricity with the lubrication of H3PO4 solution in vacuum (highest vacuum degree <10–4 torr) for the first time by performing a pre-running process in air before running in vacuum. The stable water-based superlubricity was sustainable in vacuum (0.02 torr) for 14 h until the test was stopped by the user for non-experimental factor. A further analysis suggested that the superlubricity may be attributed to the phosphoric acid–water network formed in air, which can efficiently lock water molecules in the liquid lubricating film even in vacuum owing to the strong hydrogen bond interaction. Such capability to lock water is strongly affected by the strength of hydrogen bond and environmental conditions. The realization of water-based superlubricity with H3PO4 solution in vacuum can lead to its application in space environment.
Insight into macroscale superlubricity of polyol aqueous solution induced by protic ionic liquid

Zhiwen Zheng,Xiaolong Liu,Hongxiang Yu,Haijie Chen,Dapeng Feng,Dan Qiao

DOI: https://doi.org/10.1007/s40544-021-0563-8

IF: 4.924

2022-04-12

Friction

Abstract:Abstract Currently, macroscale liquid superlubricity remains limited to low applied loads and typical ceramic friction pairs. In this study, a robust macroscale superlubricity with a coefficient of friction (COF) of approximately 0.006 is realized at the bearing steel interface induced by protic ionic liquids (ILs) in propylene glycol aqueous solution, and the lubrication system exhibits excellent anti-corrosion properties. Results show that superlubricity can be achieved by employing ILs with longer alkyl chains over a wide load ( 700 r/min) range. By systematically investigating factors affecting superlubricity, including the IL structure, ionization degree, test conditions, polyol, water-to-alcohol ratio, and lubrication state, the superlubricity mechanism is discussed. Notably, a thicker and denser stern layer can be formed using ILs with longer alkyl chains, which participates in the tribochemical reaction with the metal substrate to form a tribofilm during rubbing. The hydrogen bond network layer formed by the hydrogen ion and polycol aqueous solution can withstand high applied loads. Water can be used to reduce the shear stress of polyols, and enable superlubricity to be achieved under high-speed rotations. Moreover, an inevitable running-in period serves as a dispersing contact stress and dynamically forms a lubricating film, where the lubrication state locates mixed lubrication and then transforms into boundary lubrication as the roughness of the contact surface increases. This study is expected to significantly promote the development and application of superlubricity in the engineering field.

engineering, mechanical
Macroscale Superlubricity with Ultralow Wear and Ultrashort Running-In Period (∼1 s) through Phytic Acid-Based Complex Green Liquid Lubricants

Changhe Du,Tongtong Yu,Liqiang Zhang,Haoyu Deng,Ruilin Shen,Xiaojuan Li,Yange Feng,Daoai Wang

DOI: https://doi.org/10.1021/acsami.2c22402

2023-02-08

Abstract:Liquid superlubricity has attracted much attention, due to its ability to significantly reduce friction on the macroscale. However, the severe wear caused by the long running-in period is still one of the bottlenecks restricting the practical application of liquid superlubricating materials. In this work, the obtained polyethylene glycol-phytic acid (PEG-PA) composite liquid lubricants showed outstanding superlubricating properties (μ ≈ 0.006) for Si3N4/glass friction pairs with an ultrashort running-in period (∼1 s) under high Hertzian contact pressure of ∼758 MPa. More importantly, even after up to 12 h (∼700 m of travel), only about 100 nm deep wear scars were found on the surface of the glass sheet (wear rate = 2.51× 10-9 mm3 N-1 m-1). From the molecular point of view, the water molecules anchored between the two friction pairs have extremely low shear force during the friction process, and the strong hydrogen bond interaction between PEG and PA greatly improves the bearing capacity of the lubricant. This work addresses the challenge of liquid superlubricant simultaneously exhibiting low shear force and high load-carrying capacity and makes it possible to obtain liquid superlubrication performance with an extremely short running-in time.
Gradual Degeneration of Liquid Superlubricity: Transition from Superlubricity to Ordinary Lubrication, and Lubrication Failure

Chen Xiao,Jinjin Li,Jian Gong,Lei Chen,Jiyang Zhang,Linmao Qian,Jianbin Luo

DOI: https://doi.org/10.1016/j.triboint.2018.10.008

IF: 5.62

2019-01-01

Tribology International

Abstract:The step-by-step evolution of the friction coefficient and substrate damage during the superlubricity degeneration of Si3N4/glass pair lubricated with H3PO4 solution was investigated. The experimental results indicate that the degeneration process experiences two stages after superlubricity failure. The superlubricity state initially degenerates to the ordinary lubrication state, gradually destabilizes, and eventually fails. Further analysis demonstrates that superlubricity degeneration is mainly attributed to serious substrate damage; however, the subsequent lubrication failure is mainly caused by the insufficient amount of lubricant. Moreover, load, not speed, plays a pivotal role in the wear behavior of substrate surface and further affects the superlubricity stability. The results may reveal the degeneration mechanism of liquid superlubricity and optimize the operation and design of superlubricant systems.
Controllable Superlubricity System of Polyalkylene Glycol Aqueous Solutions under Various Applied Conditions

Wenrui Liu,Hongdong Wang,Yuhong Liu,Caixia Zhang,Jianbin Luo

DOI: https://doi.org/10.1002/mame.202000141

2020-01-01

Macromolecular Materials and Engineering

Abstract:It has been recently demonstrated that the superlubricity behavior of polyalkylene glycol (PAG) aqueous solutions can be achieved in a wide variety of applied conditions. However, certain parameters are expected to be adjusted further to achieve a more controllable superlubricity system. Herein, it is demonstrated that an ultralow friction coefficient can be obtained by concentrated PAG aqueous solutions (80 wt% HB-260) as the contact pressure becomes relatively low (37 MPa). Meanwhile, the superlubricity state can be adjusted in a timely manner by adjusting the relative sliding speed. Here, the viscosity of the PAG aqueous solution (determined by its concentration and molecular weight) and applied conditions, including contact pressure and relative sliding speed, are considered as critical parameters influencing the lubricating performance. According to the theoretical analysis, the superlubricity state is confirmed and a fitted superlubricity region is proposed, which provides a comprehensive guide for achieving controllable superlubricity in the future.
Superlubricity Behavior with Phosphoric Acid-Water Network Induced by Rubbing

Jinjin Li,Chenhui Zhang,Jianbin Luo

DOI: https://doi.org/10.1021/la201535x

IF: 3.9

2011-01-01

Langmuir

Abstract:In present work, a superlubricity phenomenon of phosphoric acid (H(3)PO(4)) was found under ambient conditions. An ultralow friction coefficient of about 0.004 between glass/Si(3)N(4) and sapphire/sapphire tribopairs was obtained under the lubrication of a phosphoric acid aqueous solution (pH 1.5) at high contact pressure (the maximum pressure can reach about 1.65 GPa) after a running-in period of about 600 s. The experimental results indicate that the superlow friction state was very stable for more than 3 h. In such a state, solidlike films formed on the two sliding surfaces, which are hydrates of phosphoric acid with a hydrogen-bonded network according to the Raman spectrum. The superlubricity mechanism is mainly attributed to the hydrogen bond effect that forms a hydrated water layer with low shearing strength, and the dipole-dipole effects that form an interfacial Coulomb repulsion force also make some contributions to low friction. This work may help us to introduce a new approach to superlubricity and may lead to the wide application of superlubricity in future technological and biomedical areas.
Superlubrication obtained with mixtures of hydrated ions and polyethylene glycol solutions in the mixed and hydrodynamic lubrication regimes

Tianyi Han,Shuang Yi,Chenhui Zhang,Jinjin Li,Xinchun Chen,Jianbin Luo,Xavier Banquy

DOI: https://doi.org/10.1016/j.jcis.2020.06.095

IF: 9.9

2020-01-01

Journal of Colloid and Interface Science

Abstract:Hypothesis: Superlubricity is known to dramatically reduce frictional energy consumption and to improve service life of mechanical devices and biological systems. However, reduction of wear during the running-in period of friction pairs, especially under high contact pressures, still remains an unresolved issue affecting all machines. Experiments: Here the lubrication, adsorption, and conformational properties of hydrated ions and polyethylene glycol (PEG) mixtures were evaluated at different mass fractions and concentrations of PEG and salts by ball-on-disc tribometer, zeta-potential, quartz crystal microbalance with dissipation (QCM-D), and dynamic light scatting (DLS) analyses. Findings: These mixtures exhibited superlubricity between Si3N4 and sapphire surfaces in a wide range of concentrations and ions valency. Interestingly, a running-in phase shorter than 1 min and low wear rate of 1.85 mu m(3) /(N.m) were observed at contact pressures up to 555 MPa, significantly higher to earlier findings. PEG chains retain random coils filling the bulk of the interfacial film without strongly adsorbing on the interfaces but significantly increasing the viscosity of lubricating film, thereby favoring hydrodynamic lubrication. Hydrated ions are strongly adsorbed on the negatively charged ceramic surfaces, ensuring a sustained hydration effect maintaining superlubricity. The outstanding lubrication characteristics of the PEG/ions mixtures were attributed to the synergistic action of hydration and hydrodynamic lubrication, which appears as a promising avenue for developing new green lubricants and has implications for industrial and biological applications. (C) 2020 Elsevier Inc. All rights reserved.
Effects of Abrasive Particles on Liquid Superlubricity and Mechanisms for Their Removal

Xiangli Wen,Pengpeng Bai,Yuanzhe Li,Hui Cao,Shaowei Li,Bin Wang,Jingbo Fang,Yonggang Meng,Liran Ma,Yu Tian

DOI: https://doi.org/10.1021/acs.langmuir.0c03607

IF: 3.9

2021-01-01

Langmuir

Abstract:Liquid superlubricity results in a near-frictionless lubrication state, which can greatly reduce friction and wear under aqueous conditions. However, during the running-in process, a large number of abrasive particles are generated, and because these may lead to a breakdown in superlubricity performance, they should be effectively removed. In this paper, the morphology, size, and composition of abrasive particles were verified using scanning electron microscopy with energy-dispersive X-ray spectroscopy, and their influence on liquid superlubricity was explored through friction tests. Subsequently, different solvents were used to remove the abrasive particles, and the optimal cleaning process was determined by macroscopic tribo-tests and microscopic analysis. Finally, droplet-spreading experiments and a force-curve analysis were carried out to understand the abrasive-particle removal mechanism by different solvents. We found that SiO2 was the main component in the abrasive particles, and micron-sized SiO2 particles resulted in random "wave peaks" in the coefficient of friction and, thus, the superlubricity. Absolute ethanol + ultrapure water was determined to be the optimal solvent for effectively removing abrasive particles from friction-pair surfaces and helped the lubricant in exhibiting an ultralow friction coefficient for long periods of time. We proposed a "wedge" and "wrap" model to explain the abrasive-particle removal mechanism of different solvents. The SiO2 removal mechanism outlined in this study can be applied under aqueous conditions to improve the stability and durability of liquid superlubricity in practical engineering applications.
Superlubricity Achieved with Mixtures of Polyhydroxy Alcohols and Acids

Jinjin Li,Chenhui Zhang,Jianbin Luo

DOI: https://doi.org/10.1021/la400810c

IF: 3.9

2013-01-01

Langmuir

Abstract:In the present work, we show that the superlubricity can be achieved when the polyhydroxy alcohol solutions are mixed with acid solutions. The lowest friction coefficients between 0.003 and 0.006 are obtained on a traditional tribometer with a high pressure under the lubrication of these mixtures. Experimental results indicate that the superlubricity mechanism is in accordance with that under the lubrication of the mixture of glycerol and acid solutions in the study by Li et al. (Li, J. J.; :Zhang, C. H.; Ma, L. R.; Liu, Y. H.; Luo, J. B. Superlubricity achieved with mixtures of acids and glycerol. Langmuir 2013, 29, 271-275). It is also found that the superlubricity is closely dependent upon the concentration of polyhydroxy alcohol and the number of hydroxyl groups in the molecular structure of polyhydroxy alcohol. However, the number of carbon atoms and the arrangement of hydroxyl groups in the molecular structure almost have no effect on superlubricity.
Mechanism of Superlubricity Conversion with Polyalkylene Glycol Aqueous Solutions

Wenrui Liu,Hongdong Wang,Yuhong Liu,Jinjin Li,Ali Erdemir,Jianbin Luo

DOI: https://doi.org/10.1021/acs.langmuir.9b01857

IF: 3.9

2019-01-01

Langmuir

Abstract:In this study, ultralow friction coefficient (COF, mu < 0.01) was obtained through polyalkylene glycol (PAG) aqueous solutions with different molecular weights (MWs) ranging from 270 to 3930 g.mol(-1) under ambient conditions. With the increase in the MWs of PAG molecules, the threshold concentration to obtain this type of superlubric behavior gradually changed from 90 to 60 wt %. This phenomenon was closely related to the interaction between PAG chains and water molecules and the state of chemical binding In the superlubricity system, superior load-bearing Disk capacity was achieved at optimal threshold concentrations of all PAG aqueous solutions wherein multilayered adsorption layers that consisted of fully hydrated PAG molecules were formed on the sliding solid surfaces. With respect to the concentration below the threshold value, the existence of a shearing layer was indicated to play a significant role. Thus, the synergetic effect of sufficient adsorption of molecules and the unique shear rheology of the PAG aqueous solution were essential to achieve superlubricity.
Superlubricity Achieved With Mixtures Of Acids And Glycerol

Jinjin Li,Chenhui Zhang,Liran Ma,Yuhong Liu,Jianbin Luo

DOI: https://doi.org/10.1021/la3046115

IF: 3.9

2013-01-01

Langmuir

Abstract:In this work, superlubricity between glass and Si3N4 surfaces lubricated by mixtures of acid solutions and glycerol solutions has been found by using a traditional tribometer. Ultra low friction coefficients of between 0.004 and 0.006 were obtained after a running-in period. Related experiments indicate that the hydrogen ions in the mixtures play an important role in achieving superlubricity. Moreover, the ultralow friction is also closely related to the pH value of the acid and the concentration of glycerol. According to these results, the possible superlubricity mechanism has been revealed, which is attributed to a fluid-hydrated water layer between the hydrogen-bonded networks of glycerol and water molecules on the positively charged surfaces.
Superlubricity of a Mixed Aqueous Solution

Ma Zhi-Zuo,Zhang Chen-Hui,Luo Jian-Bin,Lu Xin-Chun,Wen Shi-Zhu

DOI: https://doi.org/10.1088/0256-307x/28/5/056201

2011-01-01

Chinese Physics Letters

Abstract:A super-low friction coefficient of 0.0028 is measured under a pressure of 300 MPa when the friction pair (the silicon nitride ball sliding on the silicate glass) is lubricated by the mixed aqueous solution of glycerol and boric acid. The morphorlogies of the hydroxylated glass plate are observed by an atomic force microscope (AFM) in deionized water, glycerol, boric acid and their mixed aqueous solution. Bonding peaks of the retained liquids adhered on the surface of the sliding track are detected by an infrared spectrum apparatus and a Raman spectrum apparatus. The mechanism of the superlubricity of the glycerol and boric acid mixed aqueous solution is discussed. It is deduced that the formation of the lubricant film has enough strength to support higher loads, the hydration effect offering the super lower shear resistance. Key words: superlubricity, water based lubricant, ultra-low friction
Investigations On The Mechanism Of Superlubricity Achieved With Phosphoric Acid Solution By Direct Observation

jinjin li,liran ma,shaohua zhang,chenhui zhang,yuhong liu,jianbin luo

DOI: https://doi.org/10.1063/1.4821063

IF: 2.877

2013-01-01

Journal of Applied Physics

Abstract:In this work, the contact region between a Si3N4 ball and a SiO2 plate with the lubrication of phosphoric acid solution is observed directly by an optical microscope combined with a Raman microscope to understand the superlubricity mechanism. It is found that the wear on the friction surfaces mainly occurs at the beginning of the test and nearly disappears after the friction coefficient reduces to 0.05. When the superlubricity appears (mu = 0.004), there is only a limited amount of solution available to the contact (forming starvation state), resulting in an "H" distribution surrounding the contact region. Moreover, it is observed that the hydrogen bond effect in the solution is enhanced with time going by, and finally a thin film with hydrogen bond network among H3PO4, H2PO4-, and H2O is formed on the friction surfaces, leading to the superlubricity. By employing this direct observation approach, the structure of the confined solution and the superlubricity mechanism of phosphoric acid solution are finally investigated and discussed. (C) 2013 AIP Publishing LLC.
Superlubricity between sapphire and ptfe achieved by acid

Mingming Deng,Chenhui Zhang,Jinjin Li,Jianbin Luo

2016-01-01

Abstract:1.INTRODUCTION In the physical researches, friction phenomenon that describes the force existing between relative moving surfaces paves a great challenge to the industrial production and the energy efficiency. The friction reduction or elimination in the moving mechanical system would be extremely favorable to the industrial manufacture and the sustainable development of the earth. Therefore, the phenomenon “superlubricity” [1] that refers to friction coefficient less than 0.01 has become an appealing focus in recent years. Superlubricity has been attained both between solid interfaces and across liquid medium. The carbon based materials and two-dimensional materials, such as Molybdenum disulfide [2] and diamond like carbon film (DLC) [3] have been investigated mostly to achieve solid superlubricity. Different from the mechanism of solid superlubricity, the liquid superlubricity was mainly focused on the reduction of shear strength of confined liquid between two friction surfaces. On micro-level, Raviv et al. obtained a super-low friction of alkali salt solutions between mica surfaces by surface force apparatus (SFA) [4]. The liquid superlubricity above was mainly attributed to the hydration effect, leading to the great reduction of energy dissipation in the hydration layer [5]. At macro-scale, there are also some materials found having liquid superlubricity properties. Kato found that superlubricity can be achieved when water was confined between ceramics, where the formation of silica gel provided an efficient boundary lubrication [6]. Recently phosphoric acid solution was found to achieve superlubricity with a friction coefficient of 0.004 [7]. Compared with the solid superlubricity, the water-based superlubricity is more promising for industrial application, because of its nonsensitive to environment conditions. It is interesting and feasible to explore the water-based liquid superlubricity based on other mechanisms. In the present work, we investigated the friction properties of acid solution and a super-low friction coefficient of 0.004 was achieved between polytetrafluoroethylene (PTFE) and sapphire without a running-in process. Here the friction properties were explored with different sliding velocity and pH value of the lubricant, and a further investigation on the mechanism through which superlubricity is obtained has been performed.
Recent advances and mechanism discussion of superlubrication

Jianbin Luo,Bing Shi,Linmao Qian,Shizhu Wen,Yaowu Sha

1997-01-01

Abstract:The new developments of superlubrication have been reviewed. The mechanism of superlubrication has been discussed and the new problems to be solved in this area have been proposed from the theories of superfluid at low temperature, superlubricity of the clear surfaces, ordered molecules and molecular brush, the recent advances in superlubrication have been reviewed. The mechanism of superlubrication has been discussed and the new problems which should be solved have been proposed. According to the nature of superfluid at low temperature and characteristics of the interface between liquid and solid, the possibility to achieve the superlubrication state has been discussed. Then the possibility to realize the superlubrication has been discussed according to the characteristics of the interface between liquid and solid and the nature of superfluid at low temperature.
Superlubricity: Investigation of Superlubricity Achieved by Polyalkylene Glycol Aqueous Solutions (Adv. Mater. Interfaces 19/2016)

Hongdong Wang,Yuhong Liu,Jinjin Li,Jianbin Luo

DOI: https://doi.org/10.1002/admi.201670090

IF: 5.4

2016-01-01

Advanced Materials Interfaces

Abstract:Superlubricity has attracted overwhelming attention due to the ability to provide negligible friction between sliding solid surfaces. In article 1600531 by Yuhong Liu, Jianbin Luo, and co-workers, ultralow friction coefficient (μ < 0.01) can be easily obtained by a polyalkylene glycol (PAG) aqueous solution. During the sliding process, a hydrated layer is formed by hydrogen-bonded PAG chains to lower the shear strength between two solid surfaces. Meanwhile, the mixed free water molecules effectively weaken interactions among entangled polymer chains. This finding has a significant potential in industrial applications.

Speed dependence of liquid superlubricity stability with H<sub>3</sub>PO<sub>4</sub> solution

Speed Dependence of Liquid Superlubricity Stability with H3PO4 Solution

Investigation of Superlubricity Achieved by Polyalkylene Glycol Aqueous Solutions

Temporary or Permanent Liquid Superlubricity Failure Depending on Shear-Induced Evolution of Surface Topography

Achieving macroscale superlubricity with ultra-short running-in period by using polyethylene glycol-tannic acid complex green lubricant

Water-based Superlubricity in Vacuum

Insight into macroscale superlubricity of polyol aqueous solution induced by protic ionic liquid

Macroscale Superlubricity with Ultralow Wear and Ultrashort Running-In Period (∼1 s) through Phytic Acid-Based Complex Green Liquid Lubricants

Gradual Degeneration of Liquid Superlubricity: Transition from Superlubricity to Ordinary Lubrication, and Lubrication Failure

Controllable Superlubricity System of Polyalkylene Glycol Aqueous Solutions under Various Applied Conditions

Superlubricity Behavior with Phosphoric Acid-Water Network Induced by Rubbing

Superlubrication obtained with mixtures of hydrated ions and polyethylene glycol solutions in the mixed and hydrodynamic lubrication regimes

Effects of Abrasive Particles on Liquid Superlubricity and Mechanisms for Their Removal

Superlubricity Achieved with Mixtures of Polyhydroxy Alcohols and Acids

Mechanism of Superlubricity Conversion with Polyalkylene Glycol Aqueous Solutions

Superlubricity Achieved With Mixtures Of Acids And Glycerol

Superlubricity of a Mixed Aqueous Solution

Investigations On The Mechanism Of Superlubricity Achieved With Phosphoric Acid Solution By Direct Observation

Superlubricity between sapphire and ptfe achieved by acid

Recent advances and mechanism discussion of superlubrication

Superlubricity: Investigation of Superlubricity Achieved by Polyalkylene Glycol Aqueous Solutions (Adv. Mater. Interfaces 19/2016)