Abstract:Life assessment of fretting fatigue has been studied for decades. Crack-analogy methods have been proposed for analyzing fretting fatigue of flat contact pairs. In the present work we re-consider the stress field near fretting contact pairs and study the feasibility of using known fracture parameters to assess incomplete fretting contact problems. Both analytical and FEM analysis reveal that the stress field near the discontinuous round corner of a friction pad, in which the round surface has been idealized without contacting the workpiece, is the same as that of crack tip. The stress field is described by the known stress intensity factors, KI and KII. For sticking contact these two fracture parameters are independent, whereas for the slipping contact KII is linearly correlated with KI. Therefore, the stress field around the slipping contact can be characterized only by one fracture parameter, together with friction coefficient. For the continuous contact pairs with finite round contact surface, the local stress concentrations near the contact edge are finite and can be characterized by KI and KII, either, in analogy to the blunting crack tip due to finite strains. Detailed computations confirm that using the fracture parameters to characterize the fretting contact failure is affected by both loading condition and friction pad geometry. The dominance zone around the pad corner decreases more significantly with vertical press load than the horizontal friction load. In the bi-material contact friction pair the stress field can be described by KI and KII in the same form.

K-0837 Singular Stress Field Around a Frictional Contact Edge

Stress Singularities at the Frictional Contact Interface Edge with Small Slipping.

Logarithmic Singular Stress Field in an Interface Edge Consisting of Two Bonded Dissimilar Materials Subjected to a Concentrated Couple on Apex

Stress Field near the Contact Edge in Fretting Fatigue Tests.

Computational Analysis and Characterization of Fretting Stress Fields

Order of singularity and singular stress field about an axisymmetric interface corner in three-dimensional isotropic elasticity

SingularResidual Stress Field Near the Interface Edge.

Fracture Mechanics Assessment of Stress Concentrations in Incomplete Fretting Contacts

OS11W0243 Evaluation of Crack Initiation Limit in Fretting Fatigue Based on the Singular Stress Field Near the Contact Edge

Stress intensity factors of a surface crack near an interface end

Analysis of interface crack with frictional contact between fiber and matrbi in fiber reinforced composites

A Method for Determining Elastic-Plastic Stress Singularity at the Interface Edge of Bonded Power Law Hardening Materials

On Stress Singularity at the Interface Edge Between Piezoelectric Thin Film and Elastic Substrate

Iterative Method for Determination of Elastic-Plastic Stress Singularities Near an Interface Edge

K-0839 An Experimental Study on the Singular Behavior near the Interface edge of Bonded Piezoelectric Materials

Stress Singularities on Three-Dimensional Interface Edge of Bonded Dissimilar Materials

Stress Singularity at the Edge of Fiber/Matrix Interface

Analytical Solution for Sliding Rounded-Edge Contact

Singularity at the Interface Edge of Bonded Transversely Isotropic Piezoelectric Dissimilar Materials

The Singular Stress Field and Stress Intensity Factors of A Crack Terminating at A Bimaterial Interface

The nature of edge pinning and vanishing friction in microscale structural superlubric graphite contact