Abstract:Pure vanadium dioxide (VO2) and CeOx–VO2 (1.5 < x < 2) composite thin films were grown on muscovite substrate by inorganic sol–gel process using vanadium pentaoxide and cerium(III) nitrate hexahydrate powder as precursor. The crystalline structure, morphology and phase transition properties of the thin films were systematically investigated by X-ray diffraction, Raman, X-ray photoelectron spectroscopy, FE-SEM and optical transmission measurements. High quality of the VO2 and CeOx–VO2 composite films were obtained, in which the relative fractions of +4 valence state vanadium were above 70 % though the concentrations of cerium reached 9.77 at %. However, much of cerium compounds were formed at the edge of grains and the addition of cerium resulted in more clearly defined grain boundaries as shown in SEM images. Meanwhile, the composite films exhibited excellent phase transition properties and the infrared transmittance decreased from about 70 to 10 % at λ = 4 μm bellow and above the metal–insulator phase transition temperature. The metal–insulator phase transition temperatures were quite similar with about 66 °C of the pure VO2 and CeOx–VO2 composite thin films. But hysteresis widths increased with more addition of cerium, due to the limiting effect of grain boundaries on the propagation of the phase transition. Particularly, the CeOx–VO2 composite film with an addition of 7.82 at % Ce showed a largest hysteresis width with about 20.6 °C. In addition, the thermochromic performance of visible transmittance did not change obviously with more addition of cerium.

Measurement and Characterization of CeO2-TiO2 Ion Storage Films for Electrochromic Devices

Electrochromism of titanium oxide thin films

Preparation and Electrochromic Study of Ce3+ Doped TiO2 Thin Films

Electrochemical, UV–Vis, and microscopical characteristics of sol–gel CeO2:V2O5 thin film

Study on the Electrochemical Properties of Fe[sub 2]O[sub 3]-TiO[sub 2] Films Prepared by Sol-Gel Process

Photoelectrochemical Behavior of CeO2-TiO2 Composite Nanocrystalline Porous Films

Electrochromic Properties of Sol-Gel Deposited V2o5 and Tio2-V2o5 Binary Thin Films

Structural, Optical and Electrical Properties of CeO 2 Thin Films Simultaneously Prepared by Anodic and Cathodic Electrodeposition

Transparent Conducting CeO2–SiO2 Thin Films

Effects of CeO2 Buffer Layer on the Dielectric Properties of Ba0.6Sr0.4TiO3 Thin Films Prepared by Sol–gel Processing

Sol-Gel Synthesis and Characterization of Ceox-Sio2-Tio2 Thin Films

Transparent Two-Phase Composite Oxide Thin Films with High Conductivity

Ceo2 Thin Film As A Lithium-Ion-Storage Material Fabricated by Pulsed Laser Deposition

On the preparation of TiO2-CeO2 film by sol-gel process

Characteristics of CeOx–VO 2 Composite Thin Films Synthesized by Sol–gel Process

Preparation and Ferroelectric Properties of Bi 3.4 Ce 0.6 Ti 3 O 12 Thin Films Grown by Sol-Gel Method

Transparent ion-conducting ceria-zirconia films made by sol–gel technology

Effect of Ce4+-doping on Structural and Photocatalytic Properties of Sol-gel Prepared Titanium Dioxide Thin-Films

Synthesis, Characterization, and Photocatalytic Properties of Sol-Gel Ce-TiO2 Films

Preparation and Characterization of CeO<sub>2</sub>-based Oxygen Storage Materials

Electrochromic Ultra-Thin Films Based On Cerium Polyoxometalate