Abstract:Nanoscale V2O5 films possess excellent electrochemical properties and have great potential for application in electrochromic devices. Herein, we report a novel strategy for the transformation of three-dimensionally ordered macroporous(3DOM) V2O5 films into V2O5 nanorods film using a simple low-temperature annealing treatment, in which the heterogeneous nucleation sites provided by PS colloidal sphere surface, the anisotropic bonding of V2O5, atomic rearrangement, and Ostwald ripening are all important factors affecting the morphological transformation. According to this study, during the preparation of 3DOM V2O5 films, a small number of oxygen vacancies were introduced into the V2O5 lattice, and the annealing treatment (250–400 °C, 4–8 h) controlled the concentration of oxygen vacancies. Compared with the ion storage capacity of V2O5 films prepared by conventional sol-gel dip-coating method (17.79 mC cm−2 for unannealed V2O5 films and 13.90 mC cm−2 for V2O5 films after 6 h of annealing at 350 °C), the 350°C-6h films with nanorod structure had the highest ion-storage performance, the initial value raised to 98.77 mC cm−2. Further, the cycling stability was excellent, with only a 6.1% decrease after 5000 cycles. This was because of the special nanorod structure and the presence of a certain number of gradient oxygen vacancies in the 350°C-6h film. The 350°C-6h film also had good electrochromic properties, a wide range of transmittance modulation (73.6%), and a fast response time (3.2 s for coloring and 3.9 s for bleaching). In addition, electrochromic devices (ECDs) with 350°C-6h films as both ion-storage layers and electrochromic layers have been successfully assembled, which exhibit high performance.

Electrodeposition of V<sub>2</sub>O<sub>5</sub> on TiO<sub>2</sub> nanorod arrays and their electrochromic properties

Electrodeposition of V2O5 on TiO2 nanorod arrays and their electrochromic properties

Electrodeposited Cu2O on the {101} Facets of TiO2 Nanosheet Arrays and Their Enhanced Photoelectrochemical Performance

Electrochemical and electrochromic properties of novel nanoporous NiO/V 2 O 5 hybrid film

Electrodeposition of flake-like Cu2O on vertically aligned two-dimensional TiO2 nanosheet array films for enhanced photoelectrochemical properties

Excellent Electrochromic Properties of Ti4+-Induced Nanowires V2O5 Films

Building Architecture of TiO2 Nanocrystals Embedded in Amorphous WO3 Films with Improved Electrochromic Properties

Efficient Electrochromic Materials Based on Tio2@Wo3 Core/Shell Nanorod Arrays

Analysis of structural morphological changes from 3DOM V2O5 film to V2O5 nanorods film and its application in electrochromic device

Improved Electrochromic Performance of WO3 Films with Size Controlled Nanorods

Electrochemically Deposited Cu2O on TiO2 Nanorod Arrays for Photovoltaic Application

Improved Stability of Electrochromic Devices Using Ti-doped V2O5 Film

From Amorphous Macroporous Film to 3D Crystalline Nanorod Architecture: A New Approach to Obtain High‐Performance V2O5 Electrochromism

Structural Characterization and Electrical and Optical Properties of V2o5 Films Prepared Via Ultrasonic Spraying

Constructed Tio2/Nio Core/Shell Nanorod Array For Efficient Electrochromic Application

Fabrication of WO3/TiO2 core-shell nanowire arrays: Structure design and high electrochromic performance

Hydrophilicity and Photocatalysis of Ti1−xVxO2 Films Prepared by Sol–gel Method

Vanadium Pentoxide Nanobelts and Nanorolls: from Controllable Synthesis to Investigation of Their Electrochemical Properties and Photocatalytic Activities

Electrochromic Properties of Sol-Gel Deposited V2o5 and Tio2-V2o5 Binary Thin Films

Electroactive and large area V2O5 film prepared via ultrasonic spraying

Graphene oxide assisted preparation of V 2 O 5 films for electrochromic and energy storage applications