Abstract:Doping with metal ions to enhance the electrochromic performance of single material is attracting widespread attention. In this work, undoped and nickel (Ni)-doped TiO 2 electrochromic films with different doping content (0.5, 1, and 5 wt%) were successfully prepared via hydrothermal approach combined with a spin-coated technique. The effect of Ni on the microstructure, morphology, electrochemical and electrochromic performance of TiO 2 films were deep studied by field emission scanning electron microscopy (FESEM), high-resolution transmission electron microscope (HR-TEM) and X-ray photoelectron spectroscopy (XPS) and UV–Vis–NIR spectrophotometry coupled with an electrochemical workstation. FESEM images show a porous microstructure formation in all the coated films. HR-TEM images show that all the films have a polycrystalline phase with a preferred orientation along the anatase (101) plane of TiO 2 . The anatase (101) lattice spacing of Ni-doped TiO 2 samples were gradually decreased to 0.355 nm, 0.351 nm and 0.342 nm as the doped Ni increased, respectively. XRD proves the HR-TEM result. The electrochemical analysis reveals that the appropriate 1% Ni doping presented the most remarkable electrochromic performance, including that the maximum ions diffusion coefficient of 9.65 × 10 –10 cm 2 /s, the fastest coloring/bleaching switching time of 12.75 s and 1.99 s. Moreover, the 1% Ni-doping TiO 2 electrochromic film showed superior cyclic performance–little attenuation occurred after 200 cycles, whereas the undoped sample decayed almost by half after 100 cycles. The study provided valuable insights for promoting the potential applications of nickel metal-doped electrochromic materials.

Constructed Tio2/Nio Core/Shell Nanorod Array For Efficient Electrochromic Application

Efficient Electrochromic Materials Based on Tio2@Wo3 Core/Shell Nanorod Arrays

Multicolor Electrochromic Film Based on TiO2@Polyaniline Core/Shell Nanorod Array

Silver-Decorated Tio2 Nanorod Array Films with Enhanced Photoelectrochemical and Photocatalytic Properties

Construction of TiO2@C@Prussian Blue core-shell nanorod arrays for enhanced electrochromic switching speed and cycle stability

Fabrication of WO3/TiO2 core-shell nanowire arrays: Structure design and high electrochromic performance

Hierarchical SnO2@NiO core/shell nanoflake arrays as energy-saving electrochromic materials

Electrodeposited Cu2O on the {101} Facets of TiO2 Nanosheet Arrays and Their Enhanced Photoelectrochemical Performance

Co-Doped Nio Nanoflake Array Films With Enhanced Electrochromic Properties

Cobalt Ion-Modified Titanium Oxide Nanorods: A Promising Approach for High-Performance Electrochromic Application

Dual Electrochromic Film Based on WO3/polyaniline Core/shell Nanowire Array

Building Architecture of TiO2 Nanocrystals Embedded in Amorphous WO3 Films with Improved Electrochromic Properties

One-Step Fabrication Of Nanostructured Nio Films From Deep Eutectic Solvent With Enhanced Electrochromic Performance

Improved Electrochromic Performance of Hierarchically Porous Co3O4 Array Film Through Self-Assembled Colloidal Crystal Template

Interlaced NiCoO2 nanoparticle/nanosheet films for electrochromic energy storage devices with wide-band optical modulation and robust stability

Electrochromic Properties of Ni/NiO/rGO Nanocomposite Films Prepared by a Facile Sol-Gel Technique

Fabrication of TiO2: Nb array films and their enhanced electrochromic performance

Improved electrochromic device based on mesoporous TiO2 and NiO films

High durable TiO2 electrochromic films by Ni doping

Designing TiO2/Au/Prussian blue heterostructures nanorod arrays for ultra-stable cycle and ultra-fast response electrochromism

Excellent Electrochromic Properties of Ti4+-Induced Nanowires V2O5 Films