Enhanced Thermoelectric Performance of Β-Zn4sb3 Based Composites Incorporated with Large Proportion of Nanophase Cu3SbSe4
T. H. Zou,X. Y. Qin,D. Li,L. L. Li,G. L. Sun,Q. Q. Wang,J. Zhang,H. X. Xin,Y. F. Liu,C. J. Song
DOI: https://doi.org/10.1016/j.jallcom.2013.11.049
IF: 6.2
2013-01-01
Journal of Alloys and Compounds
Abstract:Thermoelectric properties of beta-Zn4Sb3 based composites, Cu3SbSe4/beta-Zn4Sb3, incorporated with large volume fraction, f (10-20 vol.%), of p-type nanophase Cu3SbSe4 have been investigated. The results indicate that as Cu3SbSe4 with a relatively lager thermopower, S, and a greater carrier mobility, mu, is incorporated into beta-Zn4Sb3, the S of the composite system increases greatly, and at T > 500 K thermoelectric power factor (PF) becomes larger than that of the beta-Zn4Sb3 matrix due to increased mobility of the composites. Especially, for the composite system with 15 vol.% of Cu3SbSe4, an increase of similar to 30% in the PF and a reduction of similar to 40% in the total thermal conductivity are achieved at 648 K, which allow the thermoelectric figure of merit (ZT) to reach 1.23 (at 648 K), a value that is 1.6 times larger than that (0.75) of matrix, beta-Zn4Sb3 in the present study. Our results suggest that incorporation of secondary phase with larger S and greater mu in large proportion in a host material could be an easy, direct and effective way to elevate the thermoelectric performance of the host. Crown Copyright (C) 2013 Published by Elsevier B.V. All rights reserved.