Multicolor Mechanoluminescence From Lu3Al2Ga3O12: Tb, Eu for Stress and Temperature Visual Sensing
Zhiyao Zhou,Sheng Wu,Binli Xiao,Yao Xiao,Peishan Shao,Pan Zheng,Jieni Ning,Yinzhen Wang,Puxian Xiong
DOI: https://doi.org/10.1002/adom.202401993
IF: 9
2024-09-16
Advanced Optical Materials
Abstract:In this work, by altering the doping concentration of Eu3+, a color‐tunable ML compound has been prepared. A stress‐temperature dual‐mode imaging system is constructed by utilizing the different responses of Tb3+ and Eu3+ ions to stress and temperature. Calculating IR (ITb /IEu) and observing the corresponding color provide a solution for accurately obtaining real‐time stress and temperature data. It has potential application prospects in human‐computer interaction, structural safety detection, and multi‐modal information storage. Mechanoluminescence (ML) refers to the luminescence phenomenon that occurs when a material is under external mechanical stimuli. However, relying solely on stress information to obtain ML signals is prone to test errors in complex test conditions. In this work, a Tb3+/Eu3+‐doped Lu3Al2Ga3O12 multicolor ML material is reported, in which the ML color can be adjusted from white to red (CIE color coordinates: from (x = 0.313, y = 0.3293) to (x = 0.6183, y = 0.379)) by changing the Eu3+ concentration. In addition, LAGO: 0.25% Tb3+ and LAGO: 1.5% Eu3+ are physically mixed at different mass ratios, and the varied stimuli‐responsed emission characteristics of Tb3+ and Eu3+ ions are used to develop a stress and temperature dual sensing device. Stress and temperature information can be further reflected simultaneously through the blue/red emission ratio IR (ITb/IEu). As the temperature increases, the color changes from white to red (CIE color coordinates: from (x = 0.3259, y = 0.306) to (x = 0.4707, y = 0.3625)), and the relative temperature sensitivity (Sr) is as high as 1.209% K−1 at 298 K. This sensing device provides a new idea for potential structural safety monitoring, multi‐modal anti‐counterfeiting technology, etc.
materials science, multidisciplinary,optics