Abstract:In this study, a micro/nano NbC reinforcement layer was prepared on a bearing steel surface by in-situ reaction method using GCr15 bearing steel and high purity niobium plate as raw materials. The rapid diffusion of C, strong carbide formation of Nb, and both melting and mass transfer of the matrix at certain temperatures easily controlled the gradient structure in the reinforcement layer. X-rays diffraction and X-ray photoelectron spectroscopy data revealed the presence of NbC, Fe3C, α-Fe, and Cr7C3 as the main phases in the reinforcement layer. The reinforcement layer can be divided into dense and gradient layers. SEM determined the volume fraction of NbC ceramic particles in the dense layer above 90%, with structure morphology close to that of a completely dense ceramic structure. The gradient layer was composed of two long-strip structures arranged alternately, with structure I consisting of dispersed NbC ceramic particles and structure II containing NbC ceramic particles embedded in the steel matrix. At the microscopic phase interface, the enhanced phase NbC particles were in direct contact with Fe3C without producing other transition phases, and NbC/Fe3C interface presented a non-coherent interface. The macroscopic interface characterized by Electron backscatter diffraction (EBSD) analysis showed consistent crystal orientation characteristics of NbC grains in the reinforcement layer. Also, the reinforcement layer was closely combined with the steel matrix without impurity holes. The macroscopic interfacial bonding strength displayed load scoring values from 0N to 100N without serious deformation failure behavior of the reinforcement layer.

Microstructure and Hardness of NbC Coating Produced in Situ

Growth Kinetics of In Situ Fabricated Dense NbC Coatings on Gray Cast Iron

Study on NbC Particulate-Reinforced Iron Matrix Composite Produced in Situ

Microstructure and bond strength of niobium carbide coating on GCr15 prepared by in-situ hot press sintering

Investigation of the Adhesion Strength and Deformation Behaviour of in Situ Fabricated Nbc Coatings by Scratch Testing

Infiltration Casting and in Situ Fabrication of NbC Particulates – Reinforced Iron Matrix Composites

Fabrication of Niobium Carbide Coating on Niobium by Interstitial Carburization

Gradually varying mechanical properties of in situ synthesized NbC–Fe-graded composite coating

Microscopic and macroscopic interfacial studies of NbC reinforcement layer on GCr15 bearing steel surface prepared by in-situ reaction method

Refinement of Microstructure and Enhancement of Wear Resistance of Ni–Cr Cast Iron by NbC

Effect of NbC in-situ synthesis on the microstructure and properties of pre-placed WCoB-TiC coating by laser cladding

Microstructure and Wear Resistance of in Situ NbC Particles Reinforced Ni-based Alloy Composite Coating by Laser Cladding

Wear Resistance of In Situ NbC-Reinforced Laser Cladding Ni45 Coatings

Mechanical Properties and Tribological Behavior of in Situ NbC/Fe Surface Composites

Effect of in Situ NbC on Microstructure and Wear Properties of Laser Cladding Co-Based Coatings

Effect of (nbti)c Particles on the Microstructure and Hardness of High Chromium and Nickel Indefinite Chilled Cast Iron

Fabrication of Ni-Based Composite Coating Reinforced with NbC Particles by Laser Cladding

Microstructural Evolution and Wear Behaviors of NbC-reinforced Ti-based Composite Coating

Microstructure, Bonding Properties and the Basis of Pinning Effect of In-Situ NbC Reinforced Co50 Composite Coating by Plasma Cladding

Microstructure and wear properties of niobium carbide particulates gradient-distribution composite layer fabricated in situ

Effect of niobium addition on the properties and microstructure of a high chromium cast iron alloy