Fluoridation and Mechanical Properties of Hydroxyapatite with Addition of TiF<sub>3</sub>, Al<sub>2</sub>O<sub>3</sub> and Fe<sub>2</sub>O<sub>3</sub> by Sintering

Muhammad Asif,Zheng Yi Fu,Shahzad Ahmad Khan,Wei Min Wang,Hao Wang,Yu Cheng Wang,Sahibzada Shakir Rehman,Rui Fang Ma
DOI: https://doi.org/10.4028/www.scientific.net/msf.804.239
2014-01-01
Materials Science Forum
Abstract:Fluoridated composite Hydroxyapatite biomaterial was prepared by sintering the hydroxyapatite Ca10 (PO4)6. (OH)2[HA] powder with addition of titanium fluoride 30 wt. % -TiF3 and mixture of iron oxide and aluminum oxide [5 wt. %-Al2O3/Fe2O3 ; (5/1)]. The pellets were prepared by conventional sol-gel technique. The as-prepared samples were sintered at various temperatures and the effect of different temperature on grain size and mechanical properties has been investigated. The samples were sintered at various temperatures of 1100-1400 °C. After sintering, the sample’s mechanical properties such as compressive strength, bending strength, Vickers hardness were improved to be 49±0.26-103±0.26 MPa, 19.6±0.20-36.2±0.20 MPa, and 7.97±0.16-12.50±0.16 GPa with their grains size 4.76±0.10-17.63±0.10 μm and bulk densities 1.8944-2.2426 g/cm3.
What problem does this paper attempt to address?