Synthesis and the magnetoresistance effect of layered-perovskite La 2.5-x K 0.5+x Mn 2 O 7+δ (0< x <0.5) polycrystals
W. Zhong,X.S. Liu,H.Y. Jiang,L.J. Zhao,Y.W. Du,N. Zhang
DOI: https://doi.org/10.1007/s00339-002-1995-2
2003-01-01
Applied Physics A
Abstract:Polycrystalline layered-perovskites La 2.5-x K 0.5+x ·Mn 2 O 7+δ (0<x<0.5) have been prepared by a modified sol-gel method and their structures, and magnetic and electric properties have been studied. Experimental results show that these materials exhibit ferromagnetic-to-paramagnetic phase transitions at 200, 225, 235, 247, and 253 K for x=0.05, 0.15, 0.25, 0.35, and 0.45, respectively. A large deviation between the metal-insulator transition temperature (T ϱ ) and the magnetic transition temperature (T C ) is observed, and a large magnetoresistance (MR) effect with Δϱ/ϱ 0 of ∼40% at 12 kOe is obtained over a wide temperature range. These behaviors are quite different from those observed in the well-knownABO 3 -type perovskite manganites.