Optimization of Planar Flow Melt Spinning Process for Producing Thin, Wide, and Continuous Amorphous Ribbons of Fe73.5Si13.5B9Nb3Cu1 Alloys
Meenuga Shanthi Raju,D. Arvindha Babu,Bhaskar Majumdar,Anil Kumar Birru,M. Manivel Raja
DOI: https://doi.org/10.1007/s11665-024-10329-5
IF: 2.3
2024-11-09
Journal of Materials Engineering and Performance
Abstract:A processing map to produce thin, wide and continuous amorphous ribbons with good quality of commercial grade Fe 73.5 Si 13.5 B 9 Nb 3 Cu 1 alloy using planar flow melt spinning technique has been established. Based on the ribbon quality and continuity, three distinct regions were identified with the following characteristics: (I) discontinuous and good-quality ribbon region, (II) continuous and good-quality ribbon region and (III) continuous and porous ribbon region. A high-speed videography investigation was carried out to understand the existence of these distinct regions which revealed that stable puddle formation in the region II experiments led to the formation of thin, wide, and continuous amorphous ribbon. An unstable puddle in the region I results in discontinuous ribbon, while insufficient flow in region III causes the formation of porous ribbons. With the parameters from region II, ten experiments were carried out to establish the repeatability. The optimized parameters for this commercial grade Fe 73.5 Si 13.5 B 9 Nb 3 Cu 1 alloy are nozzle wheel gap of 0.33 mm, wheel speed of 19.63 m/s and ejection pressure of 13.8 kPa, and the resultant soft magnetic properties are coercivity of 0.007-0.01 Oe, saturation induction of 1.08-1.1 T, and permeability of 80,000-100,000, which are equivalent to the values reported for pure elements alloys.
materials science, multidisciplinary