Abstract:Polyethylene terephthalate (PET) surfaces were treated with CH 4 /CF 4 plasmas and the surface structures as well as the dynamic behaviour of the modified surfaces after water immersion were studied using angle-dependent x-ray photoelectron spectroscopy (XPS). It was found that the fluorocarbon plasma treatment resulted in the formation of some fluorine-containing groups, which improve the surface hydrophobicity of the PET films. The extent of surface modification is dependent on the molar ratio of the CH 4 /CF 4 feed gases used in the plasma. The hydrophobicity of the modified PET films decreased after they were immersed in water, partly as a result of the 'turnover' or movement of the fluorine-containing groups from the surface to the bulk. From XPS analysis, it was found that the movement of the fluorine-containing groups depends on the modified surface structures. The turnover rates can be described by a decay constant k of surface dynamics; the larger the k value, the faster the movement of the fluorine-containing groups. Experiments showed that the degree of surface modification is higher and is maintained for a longer period for CH 4 /CF 4 mixed plasmas as compared to that treated by pure CF 4 plasma. The effect of the molar ratio of CH 4 /CF 4 feed gases and its relationship with the movement of the fluorine-containing surface groups were discussed.

Study on Surface Modification of Polyethylene Terephthalate(PET) Film by RF-Ar/O<sub>2</sub> Plasma Treatment

Study on Surface Modification of Polyethylene Terephthalate(Pet) Film by Rf-Ar/O-2 Plasma Treatment

Study on Surface Modification of PET Film by Low Temperature Oxygen Plasma Treatment

Surface modification of a biomedical polyethylene terephthalate (PET) by air plasma

Wettability of Poly(Ethylene Terephthalate) Film Treated with Low-Temperature Plasma and Their Surface Analysis by Esca

Investigation of the Surface Structures and Dynamics of Polyethylene Terephthalate (pet) Modified by Fluorocarbon Plasmas

The Modification of PTFE Films Grafted Acrylic Acid with Ar Plasma

CHANGES IN SURFACE PROPERTIES OF POLY (ETHYLENE TEREPHTHALATE) TREATED WITH LOW TEMPERATURE PLASMA: EFFECT OF PRETREATMENT WITH DIMETHYLFORMAMIDE

Studies on Surface Modification of Poly(tetrafluoroethylene) Film by Remote and Direct Ar Plasma

Surface Modification on Polyethylene Terephthalate Films with 2-Methacryloyloxyethyl Phosphorylcholine.

Controllable Wettability of Poly(Ethylene Terephthlate) Film Modified by Oxygen Combined Inductively and Capacitively Coupled Radio-Frequency Plasma

Effects of Components of Plasma on Hydrophilicity Surface Modification of PET Film

Study on Hydrophilicity of Polymer Surfaces Improved by Plasma Treatment

Ar Plasma-induced Graft Polymerization of Acrylic Acid Onto PTFE Films

Study On Surface Modification Of Polytetrafluoroethylene Film By Ar Remote-Plasma

Investigation on the surface dynamics of PET treated by CF4 and CF4/CH4 plasmas. I. - By static contact angle and angle-dependent XPS techniques

Study on the surface modification of polymer films by plasma

Influence of Magnetic Field on Inner Wall Surface of Polythylene Terephthalate Tubes Modified with C2H2 Plasma

Surface Modifications of PET Induced by High Energy Ar Ion Irradiation

Surface modification of poly(ethylene terephthalate) (PET) by magnet enhanced dielectric barrier discharge air plasma

Surface Wettability and Antibacterial Effect of PET Film Treated with Oxygen Plasma Ion Implantation