Abstract:In this study, pure cobalt oxide (Co 3 O 4 ) nanoparticles were synthesized using a simple hydrothermal approach. The effect of the reducing agent and reaction temperatures of the prepared products were examined. Co 3 O 4 is formed in the as-synthesized sample, at reaction temperature 190 °C was observed in the XRD pattern. The XPS survey scan spectrum showed the distinctive peaks of the Co and O elements and their valence states. FESEM and HRTEM revealed the particles as cubical in nature. Peak associated with the elements Co and O on the EDAX spectrum demonstrated the purity of the nanoparticles. Three electrode setups were used to measure the electrochemical properties of the synthesized nanoparticles. DTA curve corresponding exothermic peak at 225 °C and the crystallization of the final product was attributed for the third weight loss of 1.5 % in the temperature range of 280 °C to 450 °C. Formation of Co 3 O 4 was confirmed by the observed XRD diffraction peaks at 2 θ = 36.83°, 59.82°, and 65.30°, which correspond to h k l planes (311), (511) and (440), respectively. The high-resolution Co2p spectra showed two prominent spin-orbital peaks, 2p 1/2 and 2p 3/2 , at 796.37 eV and 781.81 eV, respectively. The increase in temperature causes the particle size to grow ranges between 20 and 70 nm and the average particle size distribution in the TEM image is 42 nm. The integral area of the CV curve was measured during the CV measurement and as the as-prepared Co 3 O 4 electrode displays specific capacitance values of 154, 126, 81, 65, and 49 Fg −1 at various scan rates of 10, 20, 50, 70, and 100 mVs −1 , respectively.

Synthesis and Characterization of CoO<sub>2</sub> Nanosheets

Synthesis And Electrochemical Properties Of Co Doped Mno2 Framework With Nanofibrous Structure

Electrochemical synthesis and properties of CoO2, the x = 0 phase of the AxCoO2 systems (A = Li, Na)

Synthesis and Stoichiometry of Different Layered Sodium Cobalt Oxides

Synthesis and properties of CoO2, the x = 0 end member of the LixCoO2 and NaxCoO2 systems

Synthesis and Characterization of Regular Hexagonal Nico2o4 Nanosheets

Synthesis of Co3O4 nanoparticles via an ionic liquid-assisted methodology at room temperature

Wet Chemical Synthesis And Magnetic Properties Of Core-Shell Nanocolumns Of Ni(Oh)(2)@Co(Oh)(2) And Their Oxides

Cobalt hydroxide nanosheets and their thermal decomposition to cobalt oxide nanorings.

Phase- and Size-Dependent Optical and Magnetic Properties of CoO Nanoparticles

Na order and Co charge disproportionation in Na$_{x}$CoO$_{2}$

Synthesis and Characterization of CaTi2O4 (OH)2 Nanosheets for Lithium-Ion Battery

Synthesis and Physical Properties of Co3O4 Nanowires

Synthesis, Characterization And Electrochemical Properties Of Multi-Layered Porous Co3o4 Nanoparticle Assemblies

NQR and X-ray investigation of the structure of Na$_{2/3}$CoO$_{2}$ compound

Soft-chemical exfoliation route to layered cobalt oxide monolayers and its application for film deposition and nanoparticle synthesis

Experimental and theoretical investigations on the hexagonal structure of Co2O3 nanoparticles synthesized via simple precipitation method

Facile hydrothermally grown cobalt oxide (Co 3 O 4 ) nanostructures and their electrochemical performances

Synthesis of sodium cobaltate Na$_{x}$CoO$_{2}$ single crystals with controlled Na ordering

Controllable Synthesis of CoO Nanosheets and Their Magnetic Properties

Controllable hydrothermal-assisted synthesis of mesoporous Co3O4 nanosheets

Synthesis and Characterization of CoO&lt;sub&gt;2&lt;/sub&gt; Nanosheets