LiNbO3 coating improves property of LiNi0.5Mn1.5O4 for lithium-ion battery cathode materials
Jing Zhang,Xiaofeng Cai,Jinfeng Zeng,Jiayan Liang,Boxin Zheng,Manni Chen,Yujie Wang,Weimin Zhao,Wei Yang
DOI: https://doi.org/10.1007/s11581-024-05991-7
IF: 2.961
2024-12-09
Ionics
Abstract:Because of high energy density and Co-free, spinel LiNi 0.5 Mn 1.5 O 4 materials are considered as potential replacement for availably commercial cathodes like LiNi x Mn y Co z O 2 (x + y + z = 1) and LiFePO4. However, the corrosion and interfacial breakdown of electrolyte at high voltage severely limit the extensive application of LiNi 0.5 Mn 1.5 O 4 . In this paper, LiNbO 3 was used as cladding for LiNi 0.5 Mn 1.5 O 4 cathode material by convenient and feasible wet-chemical technique. The introduction of Nb 5+ into spinel structure usually replaces Mn ions at octahedral site, thus increasing the content of Mn 3+ . Improve the electronic transition channel and electronic transition carrier of LiNi 0.5 Mn 1.5 O 4 materials. Therefore, while LiNbO 3 cladding layer protects materials from HF attack, the subsurface-rich Mn 3+ is considered to boost high-rate performance. When the mass ratio of LiNbO 3 coating is 3%, the coating-modified LiNi 0.5 Mn 1.5 O 4 material exhibits the best property. The specific discharge capacity was 129.2 mAh·g −1 with 93.5% capacity retention rate after 100 cycles at 1 C, the specific discharge capacity reached 116.0 mAh·g −1 at 5 C. Compared with uncoated LiNi 0.5 Mn 1.5 O 4 material, it shows outstanding electrochemical properties.
chemistry, physical,physics, condensed matter,electrochemistry