Microstructures and properties of 45S5 bioglass® & BCP bioceramic scaffolds fabricated by digital light processing
Shuai-Bin Hua,Jin Su,Ze-Lin Deng,Jia-Min Wu,Li-Jin Cheng,Xi Yuan,Fen Chen,Hao Zhu,Da-Hu Qi,Jun Xiao,Yu-Sheng Shi
DOI: https://doi.org/10.1016/j.addma.2021.102074
IF: 11
2021-09-01
Additive Manufacturing
Abstract:<p>The porous bioceramic scaffolds require favorable mechanical properties and excellent bioactivity to promote bone repair. In this work, 45S5 bioglass® & biphasic calcium phosphate (BCP) bioceramic scaffolds with a diamond lattice structure (porosity of 70%) were manufactured accurately by digital light processing (DLP). After optimizing the solid loading of bioceramic suspension to 40 vol%, scaffolds with the minimum pore size of 400 μm were fabricated successfully under exposure energy of 12.54 mJ/cm<sup>2</sup>. In the initial stage of sintering, crystallization occurred during 45S5 bioglass® itself, bioglass also promoted hydroxyapatite (HA) decomposition to tricalcium phosphate (TCP). With extending holding time to 4 h, Si<sup>4+</sup> from 45S5 bioglass® diffused into TCP to produce Ca<sub>5</sub>(PO<sub>4</sub>)<sub>2</sub>SiO<sub>4</sub>, which could enhance the compressive strength of bioceramic scaffolds. Meanwhile, bioglass would assist the growth and roughening of ceramic grains because of the ion-diffusion from bioglass to BCP. However, as holding time extended to 6 h, abnormal grain growth and cracks occurred which would decrease compressive strength. The best value of compressive strength is 1.735 MPa at the holding time of 4 h. 45S5 bioglass® also accelerated ion exchange such as Si<sup>4+</sup> and CO<sub>3</sub><sup>2-</sup> between bioceramic and SBF solution. This kind of bioceramics may be used as bioactive scaffolds with customizable fine structures and provide potential applications in bone tissue engineering.</p>
engineering, manufacturing,materials science, multidisciplinary