Upconversion Emission Properties of Tm3+/Er3+/Yb3+ Tri-doped YF3 Powders Depending on Excitation Power, Annealed Temperature and Tm3+ Concentration
Chun-yan CAO,Wei-ping QIN,Ji-sen ZHANG,Ji-shuang ZHANG,Yan WANG,Ye JIN,Guo-dong WEI,Guo-feng WANG,Li-li WANG,Pei-fen ZHU
2007-01-01
Chinese Journal of Luminescence
Abstract:Tm~(3+)/Er~(3+)/Yb~(3+) tri-doped YF_3 powders were synthesized using a facile hydrothermal method. XRD analysis found that the powders were crystallized products.Their sizes and morphologies were character- ized by scanning electron micrographs (SEM,Hitachi S-4800),which indicated that most of the YF_3 powders were in the sizes of hundreds of nanometers.Under 980 nm excitation,we recorded the upconversion spectra at room temperature by Hitachi F-4500.From UV to IR,plenty of upconversion emissions of Tm~(3+) and Er~(3+) were observed.For Tm~(3+),～291 nm emissions come from ~1I_6→~3H_6,～347 nm from ~1I_6→~3F_4,～362 nm from ~1D2→~3H_6,～452 nm from ~1D_2→~3F_4,and～475 nm from ~1G_4→~3H_6 can be identified in the upconver- sion spectra.The upconversion emissions from Er~(3+) are:～380 nm (~4G_(11/2)→~4I_(15/2)),～408 nm(~2H_(9/2)→~4I_(15/2)),～521 nm (~2H_(11/2)→~4I_(15/2)),～537 nm (~4S_(3/2)→~4I_(15/2)),～652 nm (~4F_(9/2)→~4I_(15/2)).Therefore,cy- an-white light were observed by naked-eye under 980 nm excitation even for a low excitation power density. With increasing of the excitation power,the emissions firstly become stronger,then weaker,at last nearly dis- appear.There are some discussions on the tempe-rature-dependent upconversion emission spectra,too.Crys- tallization became well after higher temperatures annealing,and all emissions of Tm~(3+) and Er~(3+) become rela- tively stronger.Upeonversion spectra depending on Tm~(3+) concentration indicate that at relatively low Tm~(3+) concentration,Tm~(3+)-Er~(3+) interaction is dominant,and all Er~(3+) emissions become stronger for Tm~(3+) transfer energy to Er~(3+).When Tm~(3+) concentration reaches about 0.3%,Tm~(3+)-Tm~(3+) cross relaxation is dominant, and Er~(3+) emission relatively become weaker.All Tm~(3+) emissions become relatively stronger with Tm~(3+) con- eentration increasing.From the experimental results,we concluded that the YF_3 powders should be promising materials for up-conversion white light and three-dimensional solid display.