Structural Studies of (La0.52Y0.15)(Ca0.17Sr0.16)MnO3/SrTiO3 Fhin Films
H. L. Cai,X. S. Wu,Z. H. Wang,J. Gao,Neeraj Panwar,Neeraj Kumar,Vikram Sen,D. K. Pandya,S. K. Agarwal
2009-01-01
Abstract:Manganites are very interesting materials for their abundant physics and possible potential applications in industry. Well crystallized (La0.52Y0.15)(Ca0.17Sr0.16)MnO3/SrTiO3 (LYCSMO) thin films are fabricated on (001) SrTiO3 substrate with TiO2 end-surface by rf-magnetron sputtering. The cations of La,Y,Ca,Sr are disorderly interspersed occupying at A-site in ABO3 unit cell, which benefits for growing LYCSMO films. The averaged surface roughness for the film of 0.37 nm is obtained. A two-dimension growth mode is deduced. A tetragonal distortion, which may results from the distribution between the alternated a-axis unit cell and b-axis unit cell, occurs for the films grown on STO although the target of LYCSMO is confirmed to be orthorhombic with the lattice parameters of 5.4537(7) Å, 7.7063(11) Å, and 5.4601(8) Å for a, b, and c, respectively. Two set of phi scanning reflections with four-fold symmetry corresponding to (163) and (361) reflections are obtained using high resolution X-ray diffraction, which indicates the well four-fold symmetry along b-direction. Temperature dependence of resistance shows that a metal-to-insulator transition occurs at ~270K, which well higher than that of the bulk (T~220K). A relatively larger magnetoresistance is also observed in this material, which we believe that the physical properties may result from the distortion in MnO6 in the unit cell.