Abstract:Titanium dioxide doped with phosphorus was synthesized by the sol-gel method with H-3 PO4 addition. The samples were calcined at different temperatures under different atmospheres, in order to affect the Ti-O combination behavior in P-doped TiO2. The physicochemical properties of the prepared samples were investigated using TG-DTA, XRD, FTIR, XPS, TEM and UV-vis. The photocatalytic activity was evaluated by degradation of methyl orange (MO) dye under UV and visible-light irradiation. The results show that P-doped TiO2 calcined in different thermal atmosphere reveals entirely different performances. The XRD and UV-vis analysis reveal that the effect of P species in TiO2 is increased by calcining in reducing atmosphere. Further photocatalytic experiments also display that P-doped TiO2 calcined under carbothermal reduction atmosphere (R-PT) exhibits higher photocatalytic activity than that calcined in air (A-PT). The XPS results confirms that the calcining atmosphere changes the distribution concentration of surface and interface species in P-doped TiO2, such as surface oxygen and Ti3+ sites, resulting in the improved photocatalytic activity and enhanced reutilization performance of R-PT. Further mechanism study illustrates that the promoting photocatalytic activity of P-doped TiO2 are ascribed to the formation of Ti3+ sites rather than exceeding oxygen on the surface. And the carbothermal process helps to reserve these Ti3+ sites during high temperature calcination, resulting in the increased photocatalytic activity of P-doped TiO2, especially when the doping level of P species is relative low. (C) 2013 Elsevier B.V. All rights reserved.

Luminescence and photocatalytic performance of Ca1−xTiO3:Pr3+ material

A hydrothermal synthesis of Pr3+ doped mesoporous TiO2 for UV light photocatalysis.

Enhancement of Luminescent Properties of Sol-Gel-Derived BaTiO3: Pr

Synthesis and Red Luminescence of Pr3+-doped CaTiO3 Nanophosphor from Polymer Precursor

Luminescence and photocatalytic properties of bifunctional materials CaTi2O4(OH)2:Eu3+ and [CaTi2O4(OH)2–CaTiO3]:Eu3+

Effect of Sr2+ substitution for equivalent Ca2+ ions on luminescence intensity of CaTiO3 : 0.002Pr(3+)

Effect of different doped elements on visible light absorption and ultraviolet light emission on Er 3:Y 3Al 5O 12

Effect of Ca Deficiencies on the Photoluminescence of CaTiO3:Pr3+

Luminescent Properties of Pr3+ Doped (ca, Zn) TiO3: Powders and Films

(Zn,Ca) Solid-Solution Behavior and Luminescence Properties of Ca_(1-x)Zn_xTiO_3∶0.002Pr~(3+) Phosphors

Photoluminescence and its Enhancement of Pr<sup>3+</sup>-Doped BaTiO<sub>3</sub> Phosphor

Photoluminescence effects and probing phase transition of Sm3+-doped Ba(Ti0.8Hf0.2)O3-(Ba0.7Ca0.3)TiO3 phosphor prepared by hydrothermal method

Photocatalytic activity of PbTiO<sub>3</sub> nanocrystals synthesized by hydrothermal method

Bismuth and chromium co-doped strontium titanates and their photocatalytic properties under visible light irradiation

Effect of Calcined Atmosphere on the Photocatalytic Activity of P-doped TiO2

Preperation and Photoluminescent Properties of Ca2AlSi3O2N5:Sm3+ Phosphor

(Zn, Ca) solid-solution behavior and its effect on luminescence properties in Ca1-xZnxTiO3 : 0.002Pr(3+) phosphors

Tailoring lanthanide doping in perovskite CaTiO3 for luminescence applications.

Enhanced Photoluminescence of CaTiO3:Pr3+ Phosphor Films Deposited on SiO2 Buffered Si Substrates

Synthesis of Ce3+and Pr3+-Codoped SrTiO3 and Its Luminescence Properties by Sol-Gel Route

Hopping mechanisms, photoluminescence studies toward highly efficient UV-responsive Pr2MgTiO6 photocatalyst