Abstract:Low-cycle fatigue (LCF) behavior of nickel-based precipitation-strengthened superalloy GH4145/SQ was investigated systematically under fully reversed total strain amplitude control conditions at 538°C in laboratory air. It was shown that the alloy exhibited a pronounced initial fatigue hardening followed by continuous fatigue softening to failure at high strain amplitudes, while at low strain amplitudes the initial hardening was followed by a well-defined saturation stage. Microstructure observations using optical and transmission-electron microscopy revealed that slip band density increased with increasing total strain amplitudes and the size of the γ′precipitates tended to reduction due to repeated shearing by the dislocations with continuous cyclic straining. The above changes in microstructures during cycling were essentially responsible for the fatigue hardening–softening behavior of the alloy. Both optical and SEM micrographs indicated that at low strain amplitudes crack propagation was basically transgranular, while at high strain amplitudes crack propagation was essentially intergranular. Bilinear behavior with a change of slope at a plastic strain amplitude of about 0.2pct was observed in cyclic stress–strain (CSS), Coffin–Manson (C–M) and plastic strain energy–life plots. A change in the number of operating slip systems and the fracture modes with the strain amplitude employed was used to explain this two-slope characteristic. In both the companion specimens test (CST) and the incremental step test (IST) methods the alloy exhibited non-masing type behavior. It was suggested that, for the first approximation, the half-life plastic strain energy could be calculated directly according to the equation without reckoning in the non-masing behavior.

Low-Cyclic Fatigue Behavior of Peak-Aged Mg–Nd-Based Alloy

Low cycle fatigue behavior of nickel-based superalloy GH4145/SQ at elevated temperature

Fatigue deformation mechanism of the Mg–Nd alloys

A Comparison of Low-Cycle Fatigue Behavior Between the Solutionized and Aged Mg-3Nd-0.2Zn-0.5Zr Alloys

Low cycle fatigue of an extruded Mg–3Nd–0.2Zn–0.5Zr magnesium alloy

Low cycle fatigue of a rare-earth containing extruded magnesium alloy

Effect of Nd additions on fatigue characteristics of a cast Mg–Zn–Zr alloy

Influence of Heat Treatment on Cyclic Deformation and Low-Cycle Fatigue Behavior of Sand-Cast Mg–10Gd–3Y–0.5Zr Magnesium Alloy

Influence of Strain Amplitude on Low-Cycle Fatigue Behaviors of a Fourth-Generation Ni-Based Single-Crystal Superalloy at 980 °C

Low-cycle fatigue behavior of solutionized and aged WE43 magnesium alloys at room temperature

On the low cycle fatigue behaviour of an Al-Zn-Mg-Cu alloy processed via non-isothermal aging

High Cycle Fatigue Behavior and Mechanical Performance of a Novel Sand-Cast Mg-Nd-Gd Alloy: Effect of Heat Treatment

On the Low Cycle Fatigue Behaviour of an Al-Zn-Mg-Cu Alloy Processed Via Non-Isothermal Ageing

Microstructure evolution during high cycle fatigue in Mg-6Zn-1Mn alloy

Cyclic Deformation Behavior of A Heat-Treated Die-Cast Al-Mg-Si-Based Aluminum Alloy

Effect of heat treatment on strain–controlled fatigue behavior of cast Mg–Nd–Zn–Zr alloy

High cycle fatigue behavior of extruded and double-aged Mg-6Zn-1Mn alloy

Low cycle fatigue behavior and its mechanism of Al7Si-0. 3Mg alloy

Cyclic Deformation and Fatigue of Extruded ZK60 Magnesium Alloy with Aging Effects

Cyclic Deformation Behavior of a High Zinc-Containing Cast Magnesium Alloy

Strain-controlled cyclic deformation behavior of cast Mg–2.99Nd–0.18Zn–0.38Zr and AZ91D magnesium alloys