Abstract:The fatigue behavior of as-cast Mg–12%Zn–1.2%Y–0.4%Zr alloy has been investigated. The S–N curve showed that the fatigue strength at 107 cycles was 45MPa. Scanning electron microscopy observations on the surfaces of the failed and unfailed specimens (after up to 1×107 cycles) suggested that the slip bands could act as preferential sites for non-propagating fatigue crack initiation, and the I-phase could effectively retard fatigue crack propagation (FCP). The macro fracture morphology clearly indicated that the overall fracture surface was composed of three regions, i.e. a fatigue crack initiation region (Region 1), a steady crack propagation region (Region 2) and a tearing region (Region 3). High-magnification fractographs showed that only porosities can act as the crack initiation sites for all specimens. Moreover, for specimens with fatigue lifetimes lower than 2×105 cycles, the cracks mostly initiated at the subsurface or surface of the specimen. However, when the fatigue lifetime was equal to or higher than 2×105 cycles, the fatigue crack initiation sites transferred to the interior of the specimen. The maximum stress intensity factors corresponding to the transition sites between Regions 1, 2 and 3 were 2 and 4.2MPam1/2, respectively. When the maximum stress intensity factor Kmax was lower than 4.2MPam1/2, in the steady crack propagation region, due to the retarding effect of I-phase/α-Mg matrix interfaces, the fatigue cracks tended to pass the I-phase/α-Mg matrix eutectic pockets directly and propagated through the grain cells, resulting in the formation of many flat facets on the fracture surface. However, when the maximum stress intensity factor was higher than 4.2MPam1/2, in the sudden failure region, the rigid bonding of I-phase/α-Mg matrix interfaces was destroyed and the cracks preferentially propagated along the interfaces, which resulted in the fracture surface being almost completely composed of cracked I-phase/α-Mg matrix eutectic pockets. Based on microstructural observation and the fracture characteristics of the two regions, it is suggested that with an increase in crack tip driving force, the FCP mode changes from transgranular propagation to intergranular propagation.

Cyclic Deformation Behavior of a High Zinc-Containing Cast Magnesium Alloy

Strain-controlled cyclic deformation behavior of cast Mg–2.99Nd–0.18Zn–0.38Zr and AZ91D magnesium alloys

The Microstructure and Mechanical Properties of As-cast Mg-10Gd-3Y-xZn-0.6Zr (x=0, 0.5, 1 and 2 Wt%) Alloys

High-Cycle Fatigue of Mg–6Gd–3Y–0.5Zr Cast Magnesium Alloys

High-cycle Fatigue Behavior of Mg-8Li-3Al-2Zn-0.5Y Alloy under Different States

Low cycle fatigue of a rare-earth containing extruded magnesium alloy

Cyclic Deformation Behavior of a High-Strength Low-Alloy (HSLA) Magnesium Alloy with Heterostructures

Influence of Heat Treatment on Cyclic Deformation and Low-Cycle Fatigue Behavior of Sand-Cast Mg–10Gd–3Y–0.5Zr Magnesium Alloy

Fatigue Properties of Cast Magnesium Wheels

High Cycle Fatigue of Cast Mg-3Nd-0.2Zn Magnesium Alloys

Cyclic Deformation and Fatigue of Extruded ZK60 Magnesium Alloy with Aging Effects

Microstructure evolution during high cycle fatigue in Mg-6Zn-1Mn alloy

Cyclic Shear Deformation and Fatigue of Extruded Mg-Gd-Y Magnesium Alloy

A Comparison of Low-Cycle Fatigue Behavior Between the Solutionized and Aged Mg-3Nd-0.2Zn-0.5Zr Alloys

High cycle fatigue behavior of as-cast Mg96.34Gd2.5Zn1Zr0.16 alloy fabricated by semi-continuous casting

Study on high cycle fatigue behavior of gravity cast Mg-3Nd-0.2Zn-Zr magnesium alloy

The Fatigue Behavior of I-phase Containing As-Cast Mg–Zn–Y–Zr Alloy

Cyclic Deformation Behavior of a Rare-Earth Containing Extruded Magnesium Alloy: Effect of Heat Treatment

Low Cycle Fatigue Behavior of the Extruded AZ80 Magnesium Alloy under Different Strain Amplitudes and Strain Rates

Ultra-High Cycle Fatigue Behavior of the As-Extruded Magnesium Alloy Zk60

Cyclic Deformation Of Rare-Earth Containing Magnesium Alloys