Plasmonic Metal Oxide Nanocrystals via Surface Anchoring of Redox-Active Phosphorus Species

Hui Du,Yang Li,Ning Zhou,Chaodan Pu,Jinglin Yin,Xueqian Kong,He Tian,Yizheng Jin

DOI: https://doi.org/10.1021/acs.chemmater.1c01393

IF: 10.508

2021-07-02

Chemistry of Materials

Abstract:We demonstrate a general and simple postsynthetic method for the generation of plasmonic oxide nanocrystals via surface anchoring of redox-active phosphorus species. The processes are initiated by the reaction between tris(trimethylsilyl)phosphine and the surface hydroxyl groups, resulting in surface-anchored redox-active phosphorus species. The following redox reactions generate free electrons in oxide nanocrystals, accompanied by the valance-state changes of the surface-anchored P from −III to +V. The resulting nanocrystals show tunable plasmon resonance peaks in the near-infrared or mid-infrared regime. The postsynthetic redox chemistry demonstrated in this work shall inspire new design of methodologies for the development of plasmonic oxide nanocrystals.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acs.chemmater.1c01393?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acs.chemmater.1c01393</a>.Optical bandgaps of the pristine In₂O₃ and the P-In₂O₃ nanocrystals (Figure S1); Drude model fit to the extinction spectrum of the P-In₂O₃ nanocrystals (Figure S2); ATR-FTIR spectrum of the pristine In₂O₃ nanocrystal powders (Figure S3); ATR-FTIR spectra of the P-In₂O₃ nanocrystals with different annealing temperatures (Figure S4); TEM image and EDX spectrum of the etched P-In₂O₃ nanocrystals (Figure S5); EDX spectrum of the P-In₂O₃ nanocrystals (Figure S6); characterization (ATR-FTIR spectra and GC mass spectrum) of the P-In₂O₃ nanocrystal reaction system (Figure S7); the gas-phase mixture collection experiment of the reaction system (Figure S8); GC-TCD analyses of the gas existed in the surface-anchored phosphorus species redox reaction system (Figure S9); characterization (UV–vis–NIR and EDX) of the pristine In₂O₃ nanocrystals and the samples post-treated with H₃P, TBP, and TMS₃P (Figure S10); characterizations (ATR-FTIR spectra, TEM, and HRTEM) of the pristine CdO and the P-CdO nanocrystals (Figure S11); LSPR peak energy, LSPR FWHM, and Q factor of the P-In₂O₃ nanocrystals with different P/In ratios (Table S1); and descriptions of estimation of free electron density of the P-In₂O₃ nanocrystals and estimation of the percentage of P atoms taking up surface In atoms (<a class="ext-link" href="/doi/suppl/10.1021/acs.chemmater.1c01393/suppl_file/cm1c01393_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

materials science, multidisciplinary,chemistry, physical