Abstract:Monocore powder-in-tube MgB2 strands were cold-drawn and heat-treated at 600C and 700C for times of up to 71 hours and structure-property relationships examined. Drawing-induced elongation of the Mg particles led, after HT, to a textured macrostructure consisting of elongated polycrystalline MgB2 fibers separated by elongated pores. The superconducting Tc, Jc and Fp were correlated with the macrostructure and grain size. Grain size increased with HT time at both 600C and 700C. Jc and hence Fp decreased monotonically but not linearly with grain size. Overall, it was observed that at 700C, the MgB2 reaction was more or less complete after as little as 30 min; at 600C, full reaction completion did not occur until 71 h. into the HT. Transport, Jct(B) was measured in a perpendicular applied field, and the magnetic critical current densities, Jcm\bot(B) and Jcm{\phi}(B), were measured in perpendicular and parallel (axial) applied fields, respectively. Particularly noticeable was the premature dropoff of Jcm\bot(B) at fields well below the irreversibility field of Jct(B). This effect is attributed to the fibrous macrostructure and its accompanying anisotropic connectivity. Magnetic measurements with the field directed along the strand axis yielded a critical density, Jcm\bot(B), for current flowing transversely to the strand axis that was less than and dropped off more rapidly than Jct(B). In the conventional magnetic measurement, the loop currents that support the magnetization are restricted by the lower of Jct(B) and Jcm{\phi} (B). In the present case the latter, leading to the premature dropoff of the measured Jcm(B) compared to Jct(B) with increasing field. This result is supported by Kramer plots of the Jcm{\phi} (B) and Jct(B) data which lead to an irreversibility field for transverse current that is very much less than the usual transport-measured longitudinal one, Birr,t.

Effect of Heat Treatment Reaction Time on the Performance of MgB2 Wires

Effect of Heat Treatments under High Isostatic Pressure on the Transport Critical Current Density at 4.2 K and 20 K in Doped and Undoped MgB2 Wires

Possibilities of MgB2/Cu Wires Fabricated by the in-situ Reaction Technique

The Preparation of MgB 2 Conductors for Magnet Application of SMES in WST

Influences of Heat Treatment and Doping on Microstructure and Superconducting Properties of MgB2 Superconductor

Influence of the Preparation Process on Microstructure, Critical Current Density and Tc of MgB2 Powder-In-Tube Wires

Improving superconducting properties of 100 m class MgB 2 wire with 18+1 filaments produced via internal Mg diffusion process

Fabrication and Superconducting Properties of MgB2 Wires with Amorphous Carbon Doping by In-situ Powder-in-tube Method

Enhanced critical current density at high magnetic fields in MgB2 wire processed by in-situ spark plasma sintering

Fabrication and Properties of Multifilamentary MgB2 Wires by In-Situ Powder-in-tube Process

Influence of mechanical reinforcement of MgB2 wires on the superconducting properties

High performance new MgB2 superconducting hollow wires

Investigation of Layered Structure Formation in MgB2 Wires Produced by the Internal Mg Coating Process under Low and High Isostatic Pressures

Drawing induced texture and the evolution of superconductive properties with heat treatment time in powder-in-tube in-situ processed MgB2 strands

Effect of Sintering Time on Superconductivity in Mgb2

Coating Thick MgB 2 Layer on Stainless Steel Substrate

Influence of Preparation Process on Microstructure, Critical Current Density and Tc of MgB2/Fe/Cu Wires

Recent Development and Status of Ex-Situ PIT MgB 2 Wires at ASG Superconductors

Mechanical properties of reinforced MgB2 wires

High-energy ball milling and synthesi temperature study to improve superconducting properties of MgB2 ex-situ tapes and wires

EFFECT OF SINTERING TIME ON SUPERCONDUCTIVITY IN <font>MgB</font><sub>2</sub>