Abstract:Anion exchange membrane water electrolysis (AEMWE) is operated in an alkaline environment and has a similar membrane-electrode assembly (MEA) structure to that of proton exchange membrane water electrolysis (PEMWE). The use of non-noble metals as the electrocatalysts and operation at high current densities are inherently possible, so they are expected to be low-cost, high-performance candidates for next-generation water electrolysis systems. Improving the anion conductivity of the AEM and the activity of the non-precious metal catalysts is essential for the practical application of AEMWEs. 1 The non-noble electrocatalysts used in the MEA in this study were Ni 0.8 Co 0.2 O 2 and Ni 0.8 Fe 0.2 O, 3 which have a fused-aggregate network structure, and the electrolyte was a hydrocarbon-based AEM (QPAF-4) 4 , all of which were developed at the University of Yamanashi. The catalyst ink for the anodes was prepared by mixing the Ni 0.8 Co 0.2 O catalyst (University of Yamanashi) with solvent (water/methanol) and QPAF-4 (IEC = 2.0 meq g -1 , University of Yamanashi) binder solution. The anode ink was coated by using pulse-swirl-spray (PSS, Nordson) on the QPAF-4 membranes (IEC = 1.5 meq g -1 ) to make the catalyst-coated membranes (CCMs) with the anode. Catalyst inks for the cathodes was prepared by mixing Ni 0.8 Fe 0.2 O catalyst (University of Yamanashi) or Pt/CB catalyst (TEC10E50E, Tanaka Kikinzoku) with solvent (water/methanol) and QPAF-4 (IEC = 2.0 meq g -1 ) binder solution. The cathode ink was coated by using PSS on the gas diffusion layer (GDL, TGP-H-120, Toray) to make the gas diffusion electrodes (GDEs) for the cathodes. Ni mesh (Bekaert.co.jp) was used for the anode GDLs. The single cell (Figure 1, cell structure developed by Yokohama National University) performances were measured while supplying 1 M KOH at 80 °C to both electrodes. Figure 2 (a) shows the I-V performance of cells using Ni 0.8 Co 0.2 O for the anode and Ni 0.8 Fe 0.2 O or Pt/CB for the cathode. The electrolysis voltage observed for the cell with non-noble metal catalysts on both electrodes was higher than that for the cell with Pt/C on the cathode but was below 2 V at a current density of 1.2 A cm -2 . The value of the onset electrolysis voltage was nearly the same as that of the corresponding rotating disk electrode, 3 suggesting that the intrinsic performance of the cathode catalyst is being realized in the MEA. Increasing the amount of the cathodic catalyst loading scarcely affected the polarization. It is supposed that the fused-aggregate network structure of the Ni 0.8 Fe 0.2 O catalyst contributes to the favorable mass transfer. Figure 2 (b) shows the time dependence of the cell voltage of these cells. The increased loading amount improved the durability of the cathode. It is considered that the increase in the thickness of the cathode catalyst layer alleviated the damage of the GDL fibers to the membrane. These results indicate the possibility of adopting non-precious metal catalysts for both electrodes in AEMWE and thereby significantly reducing the catalyst cost. Acknowledgement This work was partially supported by NEDO of Japan through the AWE-1 project. References 1) A. Lim et al., J. Ind. Eng. Chem ., 76 , 410 (2019). 2) G. Shi et al., ACS Catal ., 12 , 14209 (2022). 3) G. Shi et al., ACS Omega , 8 , 13068 (2023). 4) H. Ono et al., J. Mater. Chem . A , 5 , 24804 (2017). Figure 1

High-performance anion exchange membrane water electrolyzers with a current density of 7.68 A cm<SUP>-2</SUP> and a durability of 1000 hours

High Performance Water Electrolysis using a Poly(fluorene phenylpropylammonium) Anion-Exchange Membrane with 2 M Aqueous KOH

Durable and Highly-Efficient Anion Exchange Membrane Water Electrolysis Using Poly(biphenyl Alkylene) Membrane

Anion Exchange Membrane Water Electrolysis at 10 A·cm‐2 Over 800 Hours

High Free Volume Polyelectrolytes for Anion Exchange Membrane Water Electrolyzers with a Current Density of 13.39 A cm−2 and a Durability of 1000 h

Reinforced poly(dibenzyl-co-terphenyl piperidinium) membranes for highly durable anion-exchange membrane water electrolysis at 2 A cm−2 for 1000 h

Engineering Robust Triazine Crosslinked and Pyridine Capped Anion Exchange Membrane for Advanced Water Electrolysis

Poly(fluorenyl alkylene)-based anion exchange membranes for high-performance water electrolysis

Anion Exchange Ionomers Enable Sustained Pure-Water Electrolysis Using Platinum-Group-Metal-Free Electrocatalysts

Reinforced Poly (dibenzyl-co-terphenyl piperidinium) Membranes for Highly Durable Anion-Exchange Membrane Water Electrolysis

Bioinspired Spatially Topological Strategy Boosts the Anion Exchange Membrane for Industrial-scale Water Electrolysis

Fluorine‐Containing Poly(Fluorene)‐Based Anion Exchange Membrane with High Hydroxide Conductivity and Physicochemical Stability for Water Electrolysis

Non-precious high entropy alloys and highly alkali-resistant composite membranes based high performance anion exchange membrane water electrolyzers

High Performance AEM Water Electrolysis with Aemion® Membranes

Performance and Durability of Membrane-Electrode Assemblies Using Non-Precious Metal Catalyst and a Hydrocarbon-Based Electrolyte for Anion Exchange Membrane Water Electrolysis

(Invited) Progress and Perspective Towards Low-Cost High-Performance Anion Exchange Membrane Water Electrolysis

Realizing Superior Durability of Water Electrolyzer Using Anion Exchange Membrane with an Interstitial Alkyl Chain: From a Single Cell to Large‐Sized 1‐cell Stack

Durable Membrane Electrode Assemblies for Proton Exchange Membrane Electrolyzer Systems Operating at High Current Densities

High Performance Anion Exchange Membrane Electrolysis Using Plasma-Sprayed, Non-Precious-Metal Electrodes

High-performance Poly(fluorenyl Aryl Piperidinium)-Based Anion Exchange Membrane Fuel Cells with Realistic Hydrogen Supply

Durable and conductive anion exchange membranes based on Poly(m-triphenyl carbazolyl piperidinium) for water electrolysis