Reinforced Poly (dibenzyl-co-terphenyl piperidinium) Membranes for Highly Durable Anion-Exchange Membrane Water Electrolysis

Ju Yeon Lee,So Young Lee

DOI: https://doi.org/10.1149/ma2024-01403119mtgabs

2024-08-09

ECS Meeting Abstracts

Abstract:Low-cost anion exchange membrane water electrolysis (AEMWE) is an attractive technology to solve global energy shortage and environmental problems. However, AEMWE suffers from poor performance and durability, leading to problems associated with the lack of qualified anion exchange membranes (AEMs). In this study, a reinforced membrane using PDTP (Poly(dibenzyl-co-terphenyl Piperidinium)) and PE (Polyethylen) was developed to improve performance and durability. Additionally, the effects of support layer and polymer membrane thickness on water electrolysis were observed. Due to the excellent electrochemical properties of filled PDTP, the prepared reinforced membranes exhibit excellent mechanical properties with tensile strength > 112 MPa, elongation at break > 84%, conductivity (96.3 mS cm −1 ), and dimensional stability (swelling). ratio < 50% at 80°C). More importantly, the AEMWE based on the reinforced membrane exhibits an outstanding current density of 4.86 A cm−2@2.0 V at 2.0 V and voltage decay rate, while simultaneously exhibiting in-situ durability of less than 1 and 2 A cm −2 for 1000 hours at 60°C. That it can be achieved. 0.02 mV h −1 and 0.1 mV h −1 , respectively. This study shows that PDTP reinforced composite membrane can effectively improve AEMWE performance and durability.