Abstract:Wire arc additive manufacturing (WAAM) technology has potential advantages in the production of large-scale aluminum alloy components. However, as-deposited Al–Cu alloys produced by WAAM often suffer from porosity defects and coarse eutectic phases distributed along the grain boundaries, resulting in poor mechanical properties and hindering the applicability of WAAM to prepare aluminum alloy components. Herein, 2219 aluminum alloy was prepared using WAAM assisted by interlayer friction stir processing (FSP). Porosity defects in the as-deposited materials were eliminated, and coarse eutectic phases were broken and dissolved into the α-Al matrix via interlayer FSP, improving the mechanical properties of the components. The specimens processed by WAAM + interlayer FSP were subjected to different thermal cycling at different locations. The top-layer stir zone (SZ) was not affected by thermal cycling during the additive manufacturing process, and mechanical properties in the SZ were superior to those in the middle region. Compared with the as-deposited materials prepared by WAAM, the yield strength (YS) and ultimate tensile strength (UTS) in the middle region along the horizontal direction of the components manufactured by WAAM + interlayer FSP increased from 118 to 143 MPa and from 255 to 277 MPa, respectively. Further, the ultimate fatigue strength increased from 97 to 139 MPa. The YS and UTS along the vertical direction were 140 and 268 MPa, respectively, which are slightly lower than those along the horizontal direction. This is due to the small overlapping between the two adjacent SZs. The partially melted zone (PMZ) between the SZs was not completely eliminated, and the θ phase in the PMZ was mostly distributed along the grain boundaries.

Effects of Interlayer Temperature on the Microstructures of Wire Arc Additive Manufactured Al-Zn-Mg-Cu Alloy: Insights into Texture Responses and Dynamic Precipitation Behaviors

Enhanced High-Temperature Strength and Ductility of Wire Arc Additive Manufactured Al-Ce-Mg Alloys with Fine Α-Al/al11ce3 Eutectics

Microstructure evolution and mechanical properties of the wire + arc additive manufacturing Al-Cu alloy

Microstructure characteristics under varying solidification parameters in different zones during CMT arc additive manufacturing process of 2319 aluminum alloy

Wire arc additive manufacturing of Al-Zn-Mg-Cu alloy: Microstructures and mechanical properties

Influence of temperature on deformation and damage mechanisms of wire + arc additively manufactured 2219 aluminum alloy

The Effect of Multiple Thermal Process on Microstructural Evolution and Mechanical Properties of Additive Manufactured Al/Steel Structure

Effect of heat treatment on the microstructure and properties of CuCrZr alloy manufactured by wire arc additive manufacturing

Microstructure evolution and mechanical properties of wire-arc additive manufactured Al–Zn–Mg–Cu alloy assisted by interlayer friction stir processing

Multiscale modelling of microstructure, micro-segregation, and local mechanical properties of Al-Cu alloys in wire and arc additive manufacturing

Microstructural and Defect Evolution during WAAM Resulting in Mechanical Property Differences for AA5356 Component

Influence of Interlayer Temperature on Microstructure and Mechanical Properties of Additively Manufactured Inconel 625

Evolution of microstructure and properties in 2219 aluminum alloy produced by wire arc additive manufacturing assisted by interlayer friction stir processing

Improved material properties of wire arc additively manufactured Al-Zn-mg-cu alloy through severe deformation interlayer friction stir processing and post-deposition heat treatment

Inhomogeneity and anisotropy of Al-Zn-Mg-Cu alloy manufactured by wire arc additive manufacturing: microstructure, mechanical properties, stress corrosion cracking susceptibility

Effect of Interlayer Temperature on Microstructure and Properties of High-Strength Low-Alloy Steel Manufactured Using Submerged-Arc Additive Manufacturing (SAAM)

Microstructure evolution and mechanical properties of wire-arc-additively manufactured Al–Cu–Mg–Ag alloy

An experimental and numerical study on the influence of interlayer time interval in wire-arc additive manufacturing process

Microstructure Evolution and Performance of AA2024 Alloy Through Wire-Arc Additive Manufacturing Under Different Heat Inputs

Effects of solution temperature on microstructure and mechanical properties of Al-Si-Mg aluminum alloy fabricated by wire-arc additive manufacturing

Modelling and Experimental Observation of the Deposition Geometry and Microstructure Evolution of Aluminum Alloy Fabricated by Wire-Arc Additive Manufacturing