The Isothermal Section of the Al–Mn–In Ternary System at 773K and Hard Magnetic Properties of MnAlIn Alloys

Shang Q. X.,Liu Y. R.,Su K. P.,Hu S. L.,Wang H. O.,Huang S.,Yang D. X.,Huo D. X.,Liu J.
DOI: https://doi.org/10.1007/s11669-021-00933-6
2021-01-01
Journal of Phase Equilibria and Diffusion
Abstract:The isothermal section of the Al-Mn-In ternary phase diagram at 773 K was investigated by powder x-ray diffraction (XRD). The 773 K isothermal section of this ternary system consists of 10 single-phase regions, 12 two-phase regions and 8 three-phase regions. Six binary compounds, i.e. Mn3In, Al8Mn5, Al11Mn4, λ-Al4Mn, μ-Al4Mn and Al6Mn in the Al-Mn-In system were confirmed to exist at 773 K. The binary compound Al12Mn is not observed at 773 K. No ternary compounds were found in this work. The compound Al8Mn5 forms a continuous series of solid solutions. The single phases α-Mn and β-Mn also form extended solid solutions. At 773 K, the maximum solid solubility of Al in γ2 (Al8Mn5), β-Mn and α-Mn are about 60.33, 36.78 and 1.54 at. % Al, respectively. Excess doping with In promotes the decomposition of the metastable τ-MnAl phase into nonmagnetic phases. The XRD result suggests that some of In atoms do not actually enter the crystal lattice of τ-MnAl. In doping improved the coercivity of the τ-MnAl alloys at the expense of saturation magnetization.
What problem does this paper attempt to address?