Electrospun Composite Polymer Electrolyte Membrane Enabled with Silica‐Coated Silver Nanowires

Huihui Gan,Shaoqiao Li,Yong Zhang,Jirong Wang,Zhigang Xue
DOI: https://doi.org/10.1002/ejic.202100710
IF: 2.551
2021-01-01
European Journal of Inorganic Chemistry
Abstract:Poly(ethylene oxide) (PEO)-based polymer electrolyte has widely been considered as a promising material for high-performance lithium metal batteries (LMBs) owing to the high safety, low cost, and excellent electrochemical stability. However, PEO-based solid polymer electrolyte (SPE) has always been suffered with a poor mechanical strength and low room-temperature ionic conductivity owing to its highly crystalline ethylene oxide (EO) chains. Especially, PEO-based SPE exhibits an unstable framework at elevated temperature (exceed melting temperature), thus leading to the poor electrochemical performances. Here, the electrospun composite polymer membrane (CPM) based on poly(vinylidene fluoride-hexafluoropropylene) (PVDF-HFP) is fabricated by introduction of silica-coated silver nanowires (AgNWs@SiO2). The PEO/LiTFSI is incorporated into the obtained PVDF-HFP/AgNWs@SiO2 CPM to form the PEO-based SPE. The composite polymer electrolyte membrane (CPEM) exhibits a high mechanical strength and wide electrochemical stability window (>5.0 V vs. Li+/Li) at 60 degrees C. The Li/CPEM/LiFePO4 cells also show a favorable cycle life at different rates and 92.7 mAh g(-1) (2 C) of discharge specific capacity at 90 degrees C. Consequently, the PVDF-HFP/AgNWs@SiO2 CPEM can exhibit an ideal application prospect for LMBs.
What problem does this paper attempt to address?