Epoxy-functionalized Ti3C2 Nanosheet for Epoxy Coatings with Prominent Anticorrosion Performance

Xiaomeng Li,Shuxue Zhou
DOI: https://doi.org/10.1016/j.porgcoat.2021.106559
IF: 6.6
2021-01-01
Progress in Organic Coatings
Abstract:The application of MXene in anticorrosion coatings has attracted recent research interest. Limited information exists on the effect of MXene functionalization on anticorrosion performance. In this work, epoxy-functionalized Ti3C2 nanosheets (E-Ti3C2) were prepared by grafting with (3-glycidyloxypropyl) trimethoxysilane and incor-porated into solvent-borne epoxy coatings with low mass fractions of 0.3 wt%, 0.5 wt% and 0.7 wt%. The anticorrosion properties of the coatings were investigated by electrochemical impedance spectroscopy and salt spray tests. The highest impedance was achieved for the 0.5 wt% E-Ti3C2 coating, at nearly three orders of magnitude higher than a pure epoxy coating. In contrast, the coating with unmodified Ti3C2 yielded an impedance improvement of approximately one order of magnitude. Salt spray tests manifested the same anti-corrosion results. The enhanced anticorrosion improvement by epoxy-functionalization should result from the better dispersibility and chemical bonding between the E-Ti3C2 and matrix. The mechanical properties and adhesion force of the coatings were also evaluated. A better scratch resistance, higher adhesion force and reduced flexibility resulted after E-Ti3C2 incorporation.
What problem does this paper attempt to address?