Abstract:Due to low density, large pores, and numerous cracks, recycled aggregate mortar has defects of lower fluidity and lower strength compared to natural aggregate mortar. In order to modify inherent defects of recycled aggregates, nanosilica (NS) with different dosages (0%, 0.6%, 1.2%, 1.8%, 2.4% and 3%) was added to recycled aggregate mortar (RNC), and 40% natural sand in RNC was replaced by recycled aggregates. Then consistency test, compressive strength test and microscopic tests (SEM, EDS and XRD) were conducted to investigate working performance and microscopic mechanism. It was found that the addition of NS can improve the flowability of RNC, and the consistency value reaches the maximum (53 mm) while NS content is 2.4%, which increases by 14% comparing to the specimen without NS. The compressive strength of RNC increases and decreases with increasing NS content in the ranges of 0–1.8% and 1.8–3% respectively, and compressive strength is 3.3 and 5.9 MPa at curing ages of 7 d and 28 d respectively while NS content is 1.8%, which increase 50% and 14% comparing to the specimen without NS. Meanwhile, the consistency value of the specimen with NS content of 1.8% is 51 mm, which is close the maximum value corresponding to NS content of 2.4%. For that, 1.8% is suggested as the optimal content of NS. Moreover, the addition of NS can reduce the brittleness index and mechanical damage degree, and enhance the energy absorption effect. Microscopic analysis reveals that NS can not only fill the inherent cracks and pores of recycled aggregates, but also promote cement hydration reaction, and more hydration products (C-S-H) can efficiently reduce the cracks and pores of recycled aggregates. It is believed that the finds of this paper can provide theoretical support for the application of recycled aggregates in practical engineering.

Effect of Nano Compound Addition on the Properties and Microstructure of Cement Mortar with Mixed Fine Recycled Aggregate

Unveil the Role of Nano-Caco3 in Early Shrinkage and Tensile Properties of Cement Paste: from Experimental Work to Modeling

Recycled Concrete Intensified by Nano-materials

Investigations on the Preparation and Mechanical Properties of the Nano-Alumina Reinforced Cement Composite

Effect Of Composite Nano-Addition On Mechanics Strength And Microstructure Of Cement Paste

Influence of Nano-Activated CaCO3-Metakaolin on Early Strength and Microstructure of Cement

Effect of Nano-Strengthening on the Properties and Microstructure of Recycled Concrete

Effect of Additives on the Rheological and Mechanical Properties of Microfine-Cement-Based Grout

Microstructure of Cement Mortar with Nano-Particles

Effect of Nano CaCO3 on the Properties of Autoclaved Aerated Concrete

Compressive strength and microscopic mechanism of nanosilica modified recycled aggregate mortar

Effect and mechanism of nano-Ca 10 (PO 4 ) 6 (OH) 2 additive on compressive strength of calcium aluminate cement at high temperature

Experimental investigation on the effect of incorporating nanomaterials on some properties of self-compacting cementitious mortar

Effects of Nano-CaCO_3 Intermediate on Physical and Mechanical Properties of Cement-based Materials

Influence of Nanoparticles on Fluidity and Mechanical Properties of Cement Mortar

Modification Effects of Carbon Nanotube Dispersion on the Mechanical Properties, Pore Structure, and Microstructure of Cement Mortar

Influence of Nano-Silicon Dioxide in the Enhancement of Surface Structure of Public Filler and Properties of Recycled Mortar

Enhanced early hydration and mechanical properties of cement-based materials with recycled concrete powder modified by nano-silica

Strengthening Effect of Nano-materials on the Compressive Strength and Microstructure of Recycled Brick Aggregate Concrete

Comparative study on mechanisms for improving mechanical properties and microstructure of cement paste modified by different types of nanomaterials

Chloride Permeability And Microstructure Of Portland Cement Mortars Incorporating Nanomaterials