Abstract:Calcium phosphate (CaP) scaffolds have been widely used as bone graft substitutes, but undesirable mechanical robustness and bioactivity greatly hamper its availability in clinic application. To address these issues, PEGylated poly (glycerol sebacate) (PEGS), a hydrophilic elastomer, was used to modify a model calcium phosphate cement (CPC) scaffold for bone regeneration in this study. The PEGS pre-polymer with PEG content from 0% to 40% was synthesized and was subsequently coated onto the pre-fabricated CPC scaffolds by facile infiltration and thermal-crosslink process. Compression strength and toughness of the CPC/PEGS composite scaffold (defined as CPX/Y, X referred to the PEG content in PEGS and Y referred to PEGS amount in final scaffold) were effectively tailored with increasing coating amount and PEG content, and CPX/Y exhibited an optimal compressive strength of 3.82 MPa and elongation at break of 13.20%, around 5-fold and 3-fold enhancement compared to the CPC. In vitro cell experiment with BMSCs as model indicated that coating and PEG-modified synchronously facilitated cell attachment and proliferation in a dose-dependent manner. Particularly, osteogenic differentiation of BMSCs on PEGS/CPC scaffold was strongly enhanced, especially for CP20/18. Further in vivo experiments confirmed that PEGS/CPC induced promoted osteogenesis in striking contrast to CPC and PGS/CPC. Collectively, hybrids scaffolds (around 18% coating amount and PEG content from 20% to 40%) with the combination of enhanced mechanical behavior and up-regulated cellular response were optimized and PEGS/CaP scaffolds can be deemed as a desirable option for bone tissue engineering.Statement of SignificanceInsufficient mechanical robustness and bioactivity still limit the availability of calcium phosphate (CaP) scaffolds in clinic application. Herein, calcium phosphate cement (CPC) scaffold, as a model CaP-matrix material, was modified with PEGylated PGS (PEGS) polymers by facile infiltration and thermal-crosslink process. Such biomimetic combination of PEGS and CaP-matrix porous scaffold was first explored, without affecting its porous structure. In this study, CPC scaffold was endowed with robust mechanical behavior and promoted bioactivity by simultaneously optimizing the amount of polymer coating and the PEG content in PGS. In rat critical-sized calvarial defects repairing, osteogenic efficacy of PEGS/CPC further demonstrated the potential for application in bone tissue regeneration. The design concept proposed in this study might provide new insights into the development of future tissue engineering materials. (C) 2016 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

A Review: Optimization for Poly(glycerol Sebacate) and Fabrication Techniques for Its Centered Scaffolds

Development of Poly(Glycerol Sebacate) and Its Derivatives: A Review of the Progress over the past Two Decades

Different methods of synthesizing poly(glycerol sebacate) (PGS): A review

Poly(Glycerol Sebacate) in Biomedical Applications—A Review of the Recent Literature

Optimized Synthesis of Biodegradable Elastomer PEGylated Poly(glycerol sebacate) and Their Biomedical Application

A Poly(glycerol Sebacate) Based Photo/thermo Dual Curable Biodegradable and Biocompatible Polymer for Biomedical Applications

Unveiling the Role of Key Parameters During Molecular Growth for Optimal Poly(glycerol Sebacate) Synthesis

Polyglycerol Sebacate Elastomer: A Critical Overview of Synthetic Methods and Characterisation Techniques

Poly(glycerol Sebacate)-Modified Polylactic Acid Scaffolds with Improved Hydrophilicity, Mechanical Strength and Bioactivity for Bone Tissue Regeneration

Poly(lactide-co-glycolide) Porous Scaffolds for Tissue Engineering and Regenerative Medicine

Porous Poly(glycerol Sebacate) (PGS) Elastomer Scaffolds for Skin Tissue Engineering

Polyetheretherketone/poly (glycolic Acid) Blend Scaffolds with Biodegradable Properties.

PEGylated Poly(glycerol Sebacate)-Modified Calcium Phosphate Scaffolds with Desirable Mechanical Behavior and Enhanced Osteogenic Capacity.

Effect of Static Tensile Stress on Enzymatic Degradation of Poly(glycerol Sebacate).

Synthesis and electrospun scaffolds preparation of poly(glycerol sebacate)

Characterization and optimization of glycerol/sebacate ratio in poly(glycerol-sebacate) elastomer for cell culture application.

Preparation and Characterization of Poly(glycerol Sebacate)/cellulose Nanocrystals Elastomeric Composites

Highly elastomeric poly(glycerol sebacate)-co-poly(ethylene glycol) amphiphilic block copolymers

Synthetic Biodegradable Functional Polymers for Tissue Engineering: a Brief Review

Preparing Biodegradable Polyurethane Porous Scaffold for Tissue Engineering Application

PGS/HAp Microporous Composite Scaffold Obtained in the TIPS-TCL-SL Method: An Innovation for Bone Tissue Engineering